| 牌号简介 About |
|---|
| 产品说明聚酯模塑料，无机填充，玻璃纤维增强，无苯乙烯，高尺寸稳定性，极轻微的后收缩，良好的机械性能，不可燃，非常好的电气性能，高温稳定性，UL列出的应用领域防爆开关，安全开关外壳，电话电子通信技术、电机夹钳板、布线装置、外壳部件、烤面包机面板、华夫铁盖、铁隔热板、烤箱条、烤箱旋钮和调节旋钮、霓虹灯管端部部件和底座 Product Description Polyester moulding compound, inorganically filled, glass fibre reinforced, styrene free, high dimensional stability, very slight post shrinkage, good mechanical properties, non flammable, very good electrical properties, high temperature stability, UL listed moulding compound 1.4 mm / V-0 (BK), 1.5 mm / V-0 (BN, GY), 1.5 mm / V-1 (WT), 3.0 mm / V-0 (BK, BN, BY). Application Areas Explosion proof switches, safety switch housings, electric motor clamp boards, wiring devices, housing parts, oven strips, oven knobs and regulator knobs, lamp parts |
产品描述 Product Description
用途：家电部件;通讯器材;开关;旋钮;外壳;
加工条件：压缩模塑
性能特点： 防火阻燃等级V-1; 防火阻燃等级V-0; 抗电弧; 热稳定性好; 尺寸稳定性好; 阻燃; 电气性好; 收缩性低; 表面光泽度好; Good surface appearance,Good Dimensional Stability,Good Electrical Properties,Low contractility,Flame Characteristics,Arc resistance,Heat Stabilized,V-1,V-0
填料：玻璃纤维
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
2.10 | g/cm³ | ISO 1183 |
|
表观密度 Apparent density |
0.92 | g/cm³ | ISO 60 |
|
收缩率 Shrinkage rate 3 |
0.13 | % | ISO 2577 |
|
吸水率 Water absorption rate |
|||
|
23℃，24hr 23℃，24hr |
13.0 | mg | ISO 62 |
|
后收缩 Post contraction 3 |
0.010 | % | ISO 2577 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
8.0 MPa，未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength 5 |
|||
|
1 mm 1 mm 5 |
kV/mm | IEC 60243-1 | |
|
相对电容率 Relative permittivity |
|||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
|||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
|||
|
解决方案 A Solution A |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
1.50 mm，白色 1.50 mm, white |
UL 94 | ||
|
1.40 mm，黑色 1.40 mm, black |
UL 94 | ||
|
1.50 mm，Brown，Grey 1.50 mm，Brown，Grey |
UL 94 | ||
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
压缩成型压力 Compression molding pressure |
MPa | ||
|
压缩成型温度 Compression molding temperature |
℃ | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
球压硬度 Ball hardness |
|||
|
H 961/30 H 961/30 |
MPa | ISO 2039-1 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
弯曲强度 bending strength 4 |
MPa | ISO 178 | |
|
压缩强度 compressive strength |
MPa | ISO 604 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Compression |
| 3 0.079 in/min |
| 4 short term, electrode layout P25mm/P25mm in transformer oil equivalent to IEC 60296 |
|
【新闻资讯】查看全部
我国曾经成为世界塑料制品消费大国
2016-01-18 相对于金属、石材、木材，塑料制品具有成本低、可塑性强等优点，在国民经济中应用广泛，塑料工业在当今世界上占有极为重要的地位，多年来塑料制品的生产在世界各地高速度发展。 前瞻产业研究院发布的《2011-2015年中国塑料制品行业产销需求与投资预测分析报告》显示，我国塑料制品产量在世界排名中始终位于前列，其中多种塑料制品产量已经位于全球首位，我国已经成为世界塑料制品生产大国。2001-2010年我国塑料制品产量年均增幅维持在15%以上，2010年我国塑料制品总产量达到5830万吨 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付