牌号简介 About |
---|
LLDPE用于重型包装袋、层压膜、工业化妆品、制药和食品包装材料。低温密封。坚固的海豹。优异的撕裂、刺穿和冲击强度。这些特性使依维林成为LLDPE包装膜的最佳选择。其优异的环境应力抗裂性、低温下良好的冲击性能和抗翘曲性也使其在注塑应用中具有吸引力。 EVALENE ® LF10181 is the resin of choice for tough flexible films. It exhibits a good balance of tensile and impact strength which makes it ideal for a wide range of film and packaging applications. FEATURES Balanced toughness and flexibility Superior stiffness Good tear resistance Meets FDA Philippines food-contact requirements Halal certified TYPICAL APPLICATIONS Flexible packaging Agricultural films Industrial liners Garment bags Trash bags Shopping bags Ice bags |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
0.918 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
动态,吹塑薄膜 Dynamic, blow molded film |
0.050 | ASTM D1894 | |
静态,吹塑薄膜 Static, blow molded film |
0.070 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
割线模量 Secant modulus 3 |
ASTM D882 | ||
1% 正割,MD:25 µm,吹塑薄膜 1% secant, MD: 25 µ m, blow molded film |
MPa | ASTM D882 | |
1% 正割,TD:25 µm,吹塑薄膜 1% secant, TD: 25 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸强度 tensile strength 4 |
ASTM D882 | ||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain 4 |
ASTM D882 | ||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
% | ASTM D882 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:25 µm,吹塑薄膜 MD: 25 µ m, blow molded film |
g | ASTM D1922 | |
TD:25 µm,吹塑薄膜 TD: 25 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25 µm,吹塑薄膜 45 °, 25 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blow(up Ratio) Blow(up Ratio) |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Density is that of the base polymer. Final density is higher due to the presence of antiblock |
3 0.98 in/min |
4 20 in/min |
【新闻资讯】查看全部
叠层式热流道模具可使注塑机提高一倍产量
2017-03-10 据了解,叠层式热流道模具与通常的单面注塑模相比,采用叠层式热流道模具能够使塑料熔液均匀地分布到两个独立的分型面之中,从而使注塑机的产量提高一倍以上。 当一个新项目还处于概念性设计阶段时,往往会忽略叠层式热流道模具如何选用的问题,因为许多模具设计商都不熟悉这种技术。与通常的单面注塑模相比,采用叠层式热流道模具能够使塑料熔液均匀地分布到两个独立的分型面之中,从而使注塑机的产量提高一倍以上。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |