牌号简介 About |
---|
RADEL R-7159预着色聚苯砜(PPSU)是专门为飞机内部应用而开发的,具有严格的颜色要求。该产品符合联邦航空局法规14CFR第25部分附录F,提供垂直燃烧阻力,极低的发烟量,并通过使用专有添加剂,在俄亥俄州立大学(OSU)的放热率方法中具有低放热值。它还产生低燃烧模式的有毒气体排放。该树脂对航空工业中发现的大多数液体(包括清洁剂和杀虫剂)具有良好的抵抗力。本产品可提供与原始设备制造商颜色标准相匹配的着色等级。它可以用于喷漆或未喷漆配置。白色:Radel R-7159 WH 70913白色:Radel R-7159 WH 7363蓝色:Radel R-7159 BU 7923灰色:Radel R-7159 GY 714 Radel® R-7159 pre-colored polyphenylsulfone (PPSU) resins have been developed for commercial aircraft interior applications with strict color requirements. The product complies with applicable FAA regulation 14CFR Part 25 Appendix F, offering vertical flammability resistance, very low smoke generation and low heat release values in the Ohio State University (OSU) rate of heat release method. It also generates low flaming-mode toxic gas emissions. The resin offers good resistance to most fluids found in the aviation industry including cleaning agents and pesticides. This product is available in pigmented grades to match OEM color standards. Available grades include: White: Radel® R-7159 WH 70913 White: Radel® R-7159 WH 7363 Blue: Radel® R-7159 BU 7923 Gray: Radel® R-7159 GY 714 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.43 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
380℃,2.16kg 380℃,2.16kg |
19 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
> 2410 | MPa | ASTM D638 |
拉伸强度 tensile strength |
|||
屈服 yield |
> 68.9 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
> 10 | % | ASTM D638 |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
OSU峰值放热速率 OSU peak heat release rate 3 |
kW/m² | FAR 25, AppF | |
OSU总放热量(2分钟) OSU total heat release (2 minutes) 3 |
kW·min/m² | FAR 25, AppF | |
垂直燃烧-60秒 Vertical combustion -60 seconds 3 |
FAR 25.853 | ||
滴液燃烧时间 Droplet combustion time |
FAR 25.853 | ||
燃烧时间 Burning time |
hr | FAR 25.853 | |
长度 length |
cm | FAR 25.853 | |
毒气排放 Toxic gas emissions 3 |
BSS 7239/ATS 1000/ABD 0031 | ||
CO CO |
ppm | BSS 7239/ATS 1000/ABD 0031 | |
HCL HCL |
ppm | BSS 7239/ATS 1000/ABD 0031 | |
HCN HCN |
ppm | BSS 7239/ATS 1000/ABD 0031 | |
HF HF |
ppm | BSS 7239/ATS 1000/ABD 0031 | |
NO+NO2 NO+NO2 |
ppm | BSS 7239/ATS 1000/ABD 0031 | |
SO2 SO2 |
ppm | BSS 7239/ATS 1000/ABD 0031 | |
烟雾密度 Smoke density 3 |
|||
Dmax,4 分钟 Dmax, 4 minutes 3 |
Ds | FAR 25, AppF |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 可燃性试验结果的目的不是为了反映这些或任何其他材料在实际火灾条件下的危险性。 |
【新闻资讯】查看全部
大橡塑公司4条密炼生产线首线通过验收
2020-09-22 搜料网资讯: 9 月 9 日, 大橡塑 4 条密炼生产线首线 通过了 广东某大型电缆企业 的现场 验货。 该项目被列为大橡塑公司深耕电线电缆行业的重点,保质保量在约定期内首线顺利研制 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |