牌号简介 About |
---|
ISPLEN® PP 030 G1E是一种中、低熔体流动速率的聚丙烯均聚物。它在机械性能和加工性能之间提供了最佳的平衡,用于生产单丝和断裂时具有高拉伸强度的胶带。本发明提供了一种适用于挤出过程和最终使用中保护聚合物的添加剂包装。典型应用:高强度单丝和绳索用胶带,德信用缠绕带采用挤压网带片挤压吹塑,推荐的熔融温度范围为190至250°C。每条生产线的加工条件应进行优化。 ISPLEN® PP 030 G1E is a medium-low melt flow rate polypropylene homopolymer. It offers an optimum balance between mechanical and processing properties for production of monofilaments and tapes with high tensile strength at break. It is formulated with an additive package suitable for protecting the polymer during extrusion process and final use. TYPICAL APPLICATIONS High tenacity monofilaments and tapes for ropes and twines Tapes for textil uses Extruded nets Strap Sheet extrusion Blow molding Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.905 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
1.7 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
34.0 | MPa | ISO 527-2 |
弯曲模量 Bending modulus |
1250 | MPa | ISO 178 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
90.0 | ℃ | ISO 75-2/B |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
年内第4个聚丙烯新牌号!蒲洁能化成功试产HP420M粒料
2021-11-11 搜料网资讯: 近日,蒲洁能化公司试生产的聚丙烯新产品HP420M粒料获得成功。这是该公司继今年开发聚丙烯EP340S、EP548T和RP344RK产品后又的一种新牌号,实现聚丙烯产品多元化,为拓展市 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |