牌号简介 About |
---|
pre-elecpe 1294是一种基于PE-HD的导电热塑性化合物。导电性是通过使用特殊的导电炭黑来实现的。除了低电阻率。PRE-ELEC® PE 1294具有良好的机械性能平衡,易于注射成型。典型应用包括大型塑料零件,如托盘、桶和容器。 PRE-ELEC®PE 1294 is a conductive thermoplastic compound based on PE-HD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® PE 1294 has an excellent balance of mechanical properties and is easy to injection mould. Typical applications include large plastic parts like pallets, drums and containers. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.996 | g/cm³ | ASTM D792 |
密度 Density |
1.01 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,10.0kg 190℃,10.0kg |
20 | g/10min | ASTM D1238 |
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
80 | g/10min | ASTM D1238 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,10.0kg 190℃,10.0kg |
g/10min | ISO 1133 | |
190℃,2.16kg 190℃,2.16kg |
g/10min | ISO 1133 | |
190℃,21.6kg 190℃,21.6kg |
g/10min | ISO 1133 | |
收缩率 Shrinkage rate |
|||
MD MD |
% | ISO 294-4 | |
MD MD |
% | ASTM D955 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A Shaw's A |
ASTM D2240 | ||
邵氏 D Shaw's D |
ASTM D2240 | ||
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A Shaw's A |
ISO 868 | ||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸强度 tensile strength |
MPa | ASTM D638 | |
屈服 yield |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
4 mm 4 mm |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,4 mm Fracture, 4 mm |
% | ISO 527-2 | |
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
4 mm 4 mm |
MPa | ISO 178 | |
4 mm 4 mm |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 2 |
|||
-20℃ -20℃ |
kJ/m² | ASTM D256 | |
-20℃ -20℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ASTM D256 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 2 |
|||
-20℃ -20℃ |
ASTM D256 | ||
-20℃ -20℃ |
ISO 179 | ||
23℃ 23℃ |
ISO 179 | ||
23℃ 23℃ |
ASTM D256 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 2 |
ISO 180 | ||
Area Area |
ASTM D256 | ||
-20℃,4.00 mm -20℃,4.00 mm |
kJ/m² | ASTM D256 | |
23℃,4.00 mm 23℃,4.00 mm |
kJ/m² | ASTM D256 | |
-20℃ -20℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D256 | ||
-20℃,4 mm -20℃,4 mm |
ASTM D256 | ||
23℃,4 mm 23℃,4 mm |
ASTM D256 | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 2 |
ISO 180 | ||
-20℃ -20℃ |
ISO 180 | ||
23℃ 23℃ |
ISO 180 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648-A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648-B | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 3 | |
-- -- |
℃ | ASTM D1525 4 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ESD STM11.11 | |
表面电阻率 Surface resistivity |
ohms | IEC 61340-2-3 | |
体积电阻率 Volume resistivity |
ohms·cm | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 4 mm thickness |
3 标准 B (120°C/h), 载荷2 (50N) |
4 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
【干货】几种可生物降解塑料的性能与应用比较研究
2020-09-18 搜料网资讯: 塑料自问世以来,广泛应用于国民经济的各个领域,如包装行业和一次性制品行业,给人类的生产和生活带来了极大的便利。然而,其巨大的使用量和废弃量导致了日益严 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |