牌号简介 About |
---|
说明:SBF0323/12HC是在高压技术下生产的高分子量低密度聚乙烯。用该产品制备的薄膜具有优异的光学性能、优异的机械性能和良好的收缩性能。该等级的最低生物基含量为95%,根据ASTM D6866测定。添加剂:卡瓦介质。抗阻塞介质。用途:固体和液体产品的自动包装;托盘用收缩膜。工艺:吹膜挤出。 Braskem PE SBF0323/12HC SBF0323/12HC is a high molecular weight LDPE produced under high pressure technology. Films obtained with this product show outstanding optical properties, excellent mechanical properties, and good shrinkage. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Additive: Slip Medium. Antiblock Medium. Applications: Automatic packaging of solid and liquid products; shrink films for pallets. Process: Blown Film Extrusion. Braskem PE SBF0323/12HC SBF0323/12HC is a high molecular weight LDPE produced under high pressure technology. Films obtained with this product show outstanding optical properties, excellent mechanical properties, and good shrinkage. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Additive: Slip Medium. Antiblock Medium. Applications: Automatic packaging of solid and liquid products; shrink films for pallets. Process: Blown Film Extrusion. Braskem PE SBF0323/12HC SBF0323/12HC is a high molecular weight LDPE produced under high pressure technology. Films obtained with this product show outstanding optical properties, excellent mechanical properties, and good shrinkage. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Additive: Slip Medium. Antiblock Medium. Applications: Automatic packaging of solid and liquid products; shrink films for pallets. Process: Blown Film Extrusion. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.923 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.32 | g/10min | ASTM D1238 |
Biobased Content Biobased Content |
95 | % | ASTM D6866 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
30.0 | MPa | ASTM D882 |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
40.0 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
TD,38 µm,吹塑薄膜 TD, 38 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,38.0 µm,吹塑薄膜 60 °, 38.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部
科技鉴定:绿色轮胎达到国际抢先程度
2017-08-11 近日,中国石油和化学工业联合会组织专家,对“轮胎用合成橡胶连续液相混炼新技术开发及应用示范”项目,进行科技成果鉴定。 这个科技项目,由怡维怡橡胶研究院王梦蛟博士提出,联合软控股份、益凯新材料和赛轮金宇共同完成。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |