牌号简介 About |
---|
Celcon® UV90Z是一种整体着色的、标称为9熔融流动速率的缩醛共聚物材料,稳定用于紫外线辐射暴露处。该材料的配方是为了防止在严重的紫外线照射下变色、褪色、粉化和机械性能变化。本产品有多种颜色可供室内汽车市场和其他应用。 Celcon® UV90Z is an integrally colored nominal 9 melt flow rate based acetal copolymer material stabilized for use where ultraviolet radiation exposure is to be encountered. The material is formulated to prevent discoloration, fading, chalking and mechanical property change in severe ultraviolet exposure. This product is available in many colors formulated for the interior automotive market and other applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.41 | g/cm³ | ASTM D792 |
密度 Density |
1.41 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
190℃,2.16 kg 190℃,2.16 kg |
8.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
1.8 | % | ASTM D955 |
MD MD |
2.2 | % | ASTM D955 |
TD TD |
% | ISO 294-4 | |
MD MD |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/1A/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2/1A/50 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ISO 11359-2 | |
MD MD |
1/℃ | ISO 11359-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
【新闻资讯】查看全部
影响模具抛光效果的要素
2016-07-13 影响模具抛光效果,主要有以下三个因素: 一、具钢的质量 表面硬度不均匀或特性上有差异往往会产生抛光困难,钢材中的各种夹杂物和气孔都不利于抛光。 二、热处理工艺 热处理在很多方面会影响到抛光性能,表面硬化钢材由于表面碳成分增加,其细微组织不利于抛光。因为钢材表面的小氧化物颗粒增加使抛光困难。钢材表面的渗碳或者脱碳都会使硬度发生变化,造成抛光上的困难。 三、抛光技术及工艺设备 不同硬度对抛光工艺的影 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |