牌号简介 About |
---|
Sarlink TPV 4100系列是专为要求苛刻的汽车和工业应用而设计的工程材料。Sarlink 4145是一种低密度、中等硬度的热塑性硫化胶,具有优异的压缩永久变形、弯曲疲劳、高低温性能。该材料可通过注射成型、吹塑和挤压加工,适用于密封件、垫圈、耐化学腐蚀软管和管道、靴子和波纹管等应用。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.958 | g/cm³ | ASTM D792 |
密度 Density |
0.960 | g/cm³ | ISO 1183 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
TD,100% 应变 TD, 100% strain |
1.30 | MPa | ASTM D412 |
MD,100% 应变 MD, 100% strain |
2.60 | MPa | ASTM D412 |
拉伸强度 tensile strength |
ISO 37 | ||
TD,100% 应变 TD, 100% strain |
1.30 | MPa | ISO 37 |
MD,100% 应变 MD, 100% strain |
MPa | ISO 37 | |
拉伸强度 tensile strength |
ASTM D412 | ||
断裂 fracture |
MPa | ASTM D412 | |
MD,断裂 MD, fracture |
MPa | ASTM D412 | |
拉伸强度 tensile strength |
ISO 37 | ||
断裂 fracture |
MPa | ISO 37 | |
MD,断裂 MD, fracture |
MPa | ISO 37 | |
拉伸应变 Tensile strain |
ASTM D412 | ||
断裂 fracture |
% | ASTM D412 | |
流量,断裂 Flow rate, fracture |
% | ASTM D412 | |
拉伸应变 Tensile strain |
ISO 37 | ||
断裂 fracture |
% | ISO 37 | |
流量,断裂 Flow rate, fracture |
% | ISO 37 | |
撕裂强度 tear strength |
|||
TD TD 2 |
kN/m | ISO 34-1 | |
TD TD |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
ASTM D395 | ||
23℃,22 hr 23℃,22 hr |
% | ASTM D395 | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395 | |
125℃,70 hr 125℃,70 hr |
% | ASTM D395 | |
压缩形变 Compression deformation |
ISO 815 | ||
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,5 秒,挤出成型 Shore A, 5 seconds, extrusion molding |
ASTM D2240 | ||
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
ASTM D2240 | ||
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A,5 秒,挤出成型 Shore A, 5 seconds, extrusion molding |
ISO 868 | ||
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
ISO 868 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 - TD Change rate of tensile strength in air - TD |
ASTM D573 | ||
135℃,1000 hr 135℃,1000 hr |
% | ASTM D573 | |
100% 应变,135℃,1000 hr 100% strain, 135 ℃, 1000 hr |
% | ASTM D573 | |
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
100% 应变,150℃,168 hr 100% strain, 150 ℃, 168 hr |
% | ASTM D573 | |
空气中拉伸强度的变化率 - TD Change rate of tensile strength in air - TD |
ISO 188 | ||
135℃,1000 hr 135℃,1000 hr |
% | ISO 188 | |
100% 应变 135℃,1000 hr 100% strain 135 ℃, 1000 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
100% 应变 150℃,168 hr 100% strain 150 ℃, 168 hr |
% | ISO 188 | |
空气中极限伸长率的变化率 - TD Change rate of ultimate elongation in air - TD |
ASTM D573 | ||
135℃,1000 hr 135℃,1000 hr |
% | ASTM D573 | |
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
在空气中断裂时拉伸应力变化 - TD Changes in tensile stress when fractured in air - TD |
ISO 188 | ||
135℃,1000 hr 135℃,1000 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
ASTM D573 | ||
邵氏 A,135℃,1000 hr Shaw A, 135 ℃, 1000 hr |
ASTM D573 | ||
邵氏 A,150℃,168 hr Shaw A, 150 ℃, 168 hr |
ASTM D573 | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
ISO 188 | ||
邵氏 A,135℃,1000 hr Shaw A, 135 ℃, 1000 hr |
ISO 188 | ||
邵氏 A,150℃,168 hr Shaw A, 150 ℃, 168 hr |
ISO 188 | ||
体积变化 Volume change |
|||
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ISO 1817 | |
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体表观粘度 - Capillary,@ 206/s Apparent viscosity of melt - Capillary, @ 206/s |
|||
200℃ 200℃ |
Pa·s | ISO 11443 | |
200℃ 200℃ |
Pa·s | ASTM D3835 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 B 方法,直角形试样(不割口) |
【新闻资讯】查看全部
长炼双氧水法制环氧丙烷成套技术通过鉴定
2022-04-10 从中国石化长岭炼化有限责任公司获悉,该公司10万吨/年双氧水法制环氧丙烷成套技术近日通过中国石化总部组织的技术鉴定,获得发明专利授权71项,其中国外专利12项、国内专利59项 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |