AMODEL A- 1565 HS是65%玻纤和矿物纤维增强的聚邻苯二甲酰胺(PPA),主要针对要求高刚度、良好尺寸稳定性,以及在高温下也能保持良好刚度的高成本效益的产品。该牌号同时具有高变形温度和弯曲模量。 - 黑色:A-1565 HS BK 324 Amodel® A-1565 HS is a 65% glass and mineral-reinforced polyphthalamide (PPA) designed to be cost-effective in applications requiring high stiffness, good dimensional stability and good retention of stiffness at elevated temperatures. This grades also exhibits a high deflection temperature and flexural modulus. Black: A-1565 HS BK 324 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.90 | g/cm³ | ISO 1183/A |
收缩率 Shrinkage rate |
|||
TD TD |
0.50 | % | ASTM D955 |
MD MD |
0.30 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.10 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
20700 | MPa | ASTM D638 |
拉伸模量 Tensile modulus |
ISO 527-2 | ||
23℃ 23℃ |
MPa | ISO 527-2 | |
100℃ 100℃ |
MPa | ISO 527-2 | |
150℃ 150℃ |
MPa | ISO 527-2 | |
175℃ 175℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
断裂,24℃ Fracture, 24 ℃ |
MPa | ISO 527-2 | |
断裂,150℃ Fracture, 150 ℃ |
MPa | ISO 527-2 | |
断裂,175℃ Fracture, 175 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
断裂 fracture |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
断裂,24℃ Fracture, 24 ℃ |
% | ISO 527-2 | |
断裂,150℃ Fracture, 150 ℃ |
% | ISO 527-2 | |
断裂,175℃ Fracture, 175 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
100℃ 100℃ |
MPa | ISO 178 | |
150℃ 150℃ |
MPa | ISO 178 | |
175℃ 175℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
100℃ 100℃ |
MPa | ISO 178 | |
150℃ 150℃ |
MPa | ISO 178 | |
175℃ 175℃ |
MPa | ISO 178 | |
压缩强度 compressive strength |
|||
13.0 mm 13.0 mm |
MPa | ASTM D695 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
ASTM E831 | ||
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
MD MD |
ASTM E831 | ||
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
黑色母知识大清点,塑料加工必备!
2016-08-11 塑料在加工生产离不开填充母料,但填充母料是一把双刃剑,其用量很有讲究。就以黑色母料而言,如果添加量过多,会增加塑料制品的的成本,而且会破坏制品的颜色;添加量过少,防老化助剂和碳黑的黑色母料不能充分融合,所以黑色母料的用量是一项重要技术。 |
黑色母知识大清点,塑料加工必备! 塑胶在生产加工生产离不了塑料填充母粒,但塑料填充母粒是一把双刃刀,其使用量很有注重。就以黑色母粒来讲,假如加上量太多,会提升塑胶制品的的成本费,并且会毁坏产品的颜色;加上量偏少,防脆化改性剂和碳黑的黑色母粒不可以充足结合,因此 黑色母粒的使用量是一项关键技术性。 黑色母专业知识大盘点,塑料造粒必不可少 现实生活中黑色母要与养儿防老改性剂相互配合应用,也恰好是这类混和配搭,使防脆化的实际效果更明显,仍在一定水平上减少了黑色母的使用量。 添加的量偏少,会导致碳黑相在产品中造成不持续的状况,在融合的交界处,塑胶分子结构的联接会很敏感,不密不可分,若遭受紫外光的直射,碳黑会很多的消化吸收产品的发热量,加快了产品的空气氧化,在这个状况下,黑色母粒的应用实际效果得不偿失,变成了产品中的残渣。 决策黑色色母粒品质的6大要素 黑色色母粒是应用碳黑来生产的,而危害黑色色母粒品质的要素,关键反映在下列六个层面: 1、散射度生碳黑是十分难解决并且污浊的化合物,它铺满了尘土、重量较轻、呈膨松状。除非是选用规模性的解决对策,不然它会搞脏设备和职工,使办公环境越来越污浊。 2、遮盖力针对用以废弃物或再造高聚物的色母粒而言,这一要素特别是在关键,在这种状况下,黑色的功效是要遮盖废弃物中的其他颜色。大顆粒碳黑的上色能力较弱,不容易遮盖别的全部在下一层的颜色,結果最后商品只获得偏移了的颜色。在熔融全过程中,恰当地先择具备高上色能力的碳黑来遮盖目前颜色的能力便是说白了的遮盖力。 3、触变性若一个色母粒自身具备优良的散射性,可是它不可以流动性进到所要模铸的原材料中,那生产的实际效果都不理想化。一般来说,用以生产色母粒的内搭环氧树脂具备较高的触变性。为了更好地降低成本,一些色母粒生产商业多次重复使用的原材料、废弃物或再生颗粒做为环氧树脂媒介。 4、相溶性假如色母粒是应用切削或再生颗粒生产出去的,那麼它很有可能带有空气污染物或别的不能熔融的高聚物。这会造成一些不能意料的、难以管束的不便,消耗了最后顾客的時间和原材料。这时候,能够采用内搭环氧树脂来生产高品质的色母粒,母料在熔融全过程中才有优良的相溶性。高品质的色母粒可应用LLDPE、LDPE、HDPE、PP、 PS、SAN、PA及其别的原材料来生产。 5、可靠性在今天的现代化经济发展中,全球性的消费者对色母粒的品质、干料的可靠性能等规定高是肯定必需的,这也是决策黑色母粒品质的第五个要素。可靠性的一个具体表现便是稳定的碳黑占比。假如碳黑的百分数是起伏的,那麼必须熔融的色母粒的总数不是同样的,要生产同一色彩的商品也不太可能。 6、颜色明暗交界线度销售市场上面有各种各样碳黑种类可用以色母粒的上色,但各种的颜色与价钱也是有非常大不一样。大顆粒碳黑比小粒子碳黑具备较低的着饱和度和不一样的背景色。大顆粒黑色色母粒适用例如塑料袋塑料薄膜生产,但不适感用以生产这些重视美观大方的商品,比如电视广告牌或必须遮挡紫外线的地区如农用机械塑料薄膜或外敷管路。 来源于:塑胶技术服务 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。