牌号简介 About |
---|
与混凝土、砖、砖石、金属或木材表面粘合的通用混凝土修补剂。预期用途:适用于修补混凝土、砖、砖石、地板或混凝土剥落的挡土墙。这种材料也能与木头和金属粘合。可用于混凝土中的锚栓。产品特点:易于混合和涂抹,可抹至1/4“或更高的抗压强度,抗水、油、溶剂和碱。 All-purpose concrete patching compound that bonds to concrete, brick, masonry, metal, or wood surfaces. Intended Use: Ideal for patching concrete, brick, masonry, floors, or retaining walls where the concrete has spalled. The material will also bond to wood and metal. Can be used to anchor bolts in concrete. Product Features: Easy to mix and apply Trowelable to 1/4" or more High compressive strength Resistant to water, oils, solvents, and alkalis |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固体含量 Solid content |
|||
by Volume by Volume |
100 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
树脂 resin |
按重量计算的混合比: 5.5 | ||
硬化法 Hardening method |
按重量计算的混合比: 1.0 | ||
储存稳定性 storage stability |
|||
24 ℃ 24 ℃ |
45 | min | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
耐热温度 Heat resistant temperature |
|||
Dry Dry |
121 | ℃ | |
Wet Wet |
℃ | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
24℃ 24℃ |
hr | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
压缩强度 compressive strength |
MPa | ASTM D695 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
可减重34%!麦格纳福特研发碳纤维复合副车架
2017-03-31 据外媒报道, 除了宝马全新的碳纤维内核车身(CarbonCore)技术,大部分由碳纤维制成的结构部件仍然被用于售价昂贵的超跑。而现在福特正在与汽车零部件供应商麦格纳合作,尝试使用这种材料研发出适用于普通汽车的汽车副车架。麦格纳和福特已经合作开发出碳纤维复合材料的汽车副车架原型,其由45个钢制零件组成,并用两个注塑件和四个额外的金属件代替了此前的副车架。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |