牌号简介 About |
---|
聚苯乙烯975 E:是一种用于挤出/热成型应用的高抗冲聚苯乙烯。975E具有良好的抗环境应力开裂(ESCR)性能,这决定了它在乳品行业中的应用,而乳品行业的应用受到高脂肪的影响。975E的哑光表面使其在各种定制板材应用中非常有用。其他特征包括良好的加工性、低光泽和FDA合规性。应用:乳制品ESCR应用热饮料盖平版印刷制冷衬垫一般信息:该材料符合21 CFR§177.1640中所述的FDA要求。本材料持有保险商实验室认可94HB;见www.ul.com上的UL文件E55470。USP六级材料安全数据表可帮助客户满足其安全需求。 Polystyrene 975E: Is a high-impact polystyrene designed for extrusion/thermoforming applications. The good environmental stress crack resistance (ESCR) properties of 975E dictate its use for dairy applications that are subjected to high butterfat. The matte finish of 975E makes it useful in a variety of custom sheet applications. Other features include excellent processability, low gloss, and FDA compliance. Application: Dairy ESCR application Hot drink lids Lithographic printing Refrigeration liners General Information: This material complies with FDA requirements as described in 21 CFR §177.1640. This material holds Underwriters Laboratory recognition 94HB; see UL File E55470 at www.UL.com. USP Class VI Material Safety Data Sheets are available to help customers satisfy their safety needs. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
2.8 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.40 to 0.70 | % | ASTM D955 |
Moisture Moisture |
< 0.10 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
1590 | MPa | ASTM D638 |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
落锤冲击 Drop hammer impact |
J | ASTM D3029 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
热变形温度 Hot deformation temperature |
|||
退火 annealing |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60° 60° |
ASTM D523 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
聚丙烯基材复合物向运用于换挡旋钮运用的TPU市场进军
2017-01-03 由于TPU的广泛应用和长期发展,换挡旋钮或许有理由用PP作以尝试,这样可以很好的控制重量以及成本,同时工艺方面也省去了预干燥流程需求。来自瑞典复合物Polykemi AB的POLYfillPP Touch grade 35025Q目前正在评估当中,有望代替应用于一家全球汽车制造商的汽车换挡的TPU材料。换挡钮的重量实现节省15%,而且其光泽度在注塑工艺上也比较容易实现。 Polykemi的POLYfill软触感材料应用的最初突破点来源于瑞士高端品牌刀具制造厂维氏刀具,维氏借 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |