牌号简介 About |
---|
高分子量高密度聚乙烯双峰膜树脂特性宽分子量分布优异撕裂强度优异冲击强度优异可加工性应用T恤袋垃圾桶内衬商品袋多壁内衬熟食包装 High Molecular Weight HDPE Bimodal Film Resin Characteristics Broad molecular weight distribution Excellent tear strength Exceptional impact strength Excellent processability Applications T-shirt sacks Trash can liners Merchandise bags Multi-wall liner Deli wrap |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.951 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.080 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
11 | g/10min | ASTM D1238 |
190℃,5.0kg 190℃,5.0kg |
0.32 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
割线模量 Secant modulus 2 |
|||
2% 正割,TD,20 µm,吹塑薄膜 2% secant, TD, 20 µ m, blow molded film 2 |
MPa | ASTM D882A | |
2% 正割,MD,20 µm,吹塑薄膜 2% secant, MD, 20 µ m, blow molded film 2 |
MPa | ASTM D882A | |
拉伸强度 tensile strength 2 |
|||
TD,断裂,20 µm,吹塑薄膜 TD, fracture, 20 µ m, blow molded film 2 |
MPa | ASTM D882A | |
TD,屈服,20 µm,吹塑薄膜 TD, yield, 20 µ m, blow molded film 2 |
MPa | ASTM D882A | |
MD,断裂,20 µm,吹塑薄膜 MD, fracture, 20 µ m, blow molded film 2 |
MPa | ASTM D882A | |
MD,屈服,20 µm,吹塑薄膜 MD, yield, 20 µ m, blow molded film 2 |
MPa | ASTM D882A | |
拉伸应变 Tensile strain 2 |
|||
TD,断裂,20 µm,吹塑薄膜 TD, fracture, 20 µ m, blow molded film 2 |
% | ASTM D882A | |
MD,断裂,20 µm,吹塑薄膜 MD, fracture, 20 µ m, blow molded film 2 |
% | ASTM D882A | |
落锤冲击 Drop hammer impact |
|||
20 µm,吹塑薄膜 20 µ m, blow molded film |
g | ASTM D1709-A | |
撕裂强度 tear strength |
|||
TD,20 µm,吹塑薄膜 TD, 20 µ m, blow molded film |
g | ASTM D1922 | |
MD,20 µm,吹塑薄膜 MD, 20 µ m, blow molded film |
g | ASTM D1922 | |
水气透过率 Water vapor transmittance |
|||
38℃,20 µm,吹塑薄膜 38 ℃, 20 µ m, blow molded film |
g/m²/24 hr | ASTM F1249 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3417 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 20 in/min |
【新闻资讯】查看全部
宜家承诺至2020年塑料产品100%可再生
2016-01-19 家具制造巨头宜家公司承诺到2020年将使100%的塑料产品都采用可再生和再生材料,但聚氨酯泡沫产品将被排除在外。 在日前于荷兰莱顿市召开的第10届生物塑料会议上,宜家可持续性产品开发人员、全球零售服务部Per Stoltz发表主题演讲,说道:“至2020年,我们所用到的塑料将全部由可再生资源或回收料制成。” 在再生材料方面,他补充说:"我们主要集中于二代原料,这类材料有望能在再生系统中得到处置。" 但是,在聚氨酯方面,尽管可以用可再生资源来生 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |