牌号简介 About |
---|
Braskem PE SLH118 SLH118是一种线性低密度聚乙烯,己烯-1共聚物,采用球化法生产。开发用于与聚乙烯混合的吹塑薄膜挤出。用该产品制备的薄膜具有良好的加工性能,具有良好的光学、机械性能和密封性。非常低的凝胶量。它含有抗氧化添加剂。该等级的最低生物基含量为84%,根据ASTM D6866测定。用途:拉伸薄膜:衬垫;低密度聚乙烯和高密度聚乙烯的混合物和一般用途的包装。其他应用:灌溉管道的混合物。化妆品和制药用柔性容器(符合USP 37)。Braskem PE SLH118说明:SLH118是线性低密度聚乙烯,己烯-1共聚物。开发用于与聚乙烯混合的吹塑薄膜挤出。用该产品制备的薄膜具有良好的加工性能,具有良好的光学、机械性能和密封性。非常低的凝胶量。它含有抗氧化添加剂。该等级的最低生物基含量为84%,根据ASTM D6866测定。用途:拉伸薄膜;衬垫;普通用途的低密度聚乙烯和高密度聚乙烯混合物和包装。其他应用:灌溉管道的混合物。工艺:薄膜挤出的推荐工艺条件约为170-210°C。最佳工艺条件将根据所用设备的类型而变化,不能作为性能保证。 Braskem PE SLH118 SLH118 is a Linear Low Density Polyethylene developed for blown film extrusion. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. It contains antioxidant additives. The minimum biobased content of this grade is 84%, determined according to ASTM D6866. Applications: Stretch films; liners; LDPE and HDPE blends and packages for general use. Others applications: blends for irrigation pipes. Flexible containers for cosmetics and pharmaceutical applications (complies with USP 37). Process: Recommended processing conditions for film extrusion about 170 - 210 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. Braskem PE SLH118 SLH118 is a Linear Low Density Polyethylene developed for blown film extrusion. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. It contains antioxidant additives. The minimum biobased content of this grade is 84%, determined according to ASTM D6866. Applications: Stretch films; liners; LDPE and HDPE blends and packages for general use. Others applications: blends for irrigation pipes. Flexible containers for cosmetics and pharmaceutical applications (complies with USP 37). Process: Recommended processing conditions for film extrusion about 170 - 210 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. Braskem PE SLH118 SLH118 is a Linear Low Density Polyethylene developed for blown film extrusion. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. It contains antioxidant additives. The minimum biobased content of this grade is 84%, determined according to ASTM D6866. Applications: Stretch films; liners; LDPE and HDPE blends and packages for general use. Others applications: blends for irrigation pipes. Flexible containers for cosmetics and pharmaceutical applications (complies with USP 37). Process: Recommended processing conditions for film extrusion about 170 - 210 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.916 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
Biobased Content Biobased Content |
84 | % | ASTM D6866 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
40.0 | MPa | ASTM D882 |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
40.0 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
弯曲模量 Bending modulus |
|||
1% 正割,TD,40 µm,吹塑薄膜 1% secant, TD, 40 µ m, blow molded film |
MPa | ASTM D790 | |
1% 正割,MD,40 µm,吹塑薄膜 1% secant, MD, 40 µ m, blow molded film |
MPa | ASTM D790 | |
落锤冲击 Drop hammer impact |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ASTM D1709 | |
撕裂强度 tear strength |
|||
TD,40 µm,吹塑薄膜 TD, 40 µ m, blow molded film |
g | ASTM D1922 | |
MD,40 µm,吹塑薄膜 MD, 40 µ m, blow molded film |
g | ASTM D1922 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部
道达尔能源加强开发伊自然资源
2021-09-18 搜料网资讯: 9月6日,在伊拉克总理的见证下,道达尔能源与伊拉克石油部、电力部及国家投资委员会签署了涵盖巴士拉地区多个项目的重要协议,致力于加强开发伊拉克的自然资源, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |