牌号简介 About |
---|
超乙烯UE672是一系列韧性好、柔韧性好、澄清度好的EVA共聚树脂。典型应用包括层压和重型薄膜以及注塑和吹塑。 Ultrathene UE672 is a series of EVA copolymer resins with good toughness, flexibility and clarity. Typical applications include laminating and heavy duty films as well as injection and blow molding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.50 | g/10min | ASTM D1238 |
醋酸乙烯含量 Vinyl acetate content |
13.5 | wt% | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
38 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:38 µm,吹塑薄膜 1% secant, MD: 38 µ m, blow molded film |
90.3 | MPa | ASTM D882 |
1% 正割,TD:38 µm,吹塑薄膜 1% secant, TD: 38 µ m, blow molded film |
91.0 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,38 µm,吹塑薄膜 MD, yield, 38 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,38 µm,吹塑薄膜 TD, yield, 38 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,屈服,38 µm,吹塑薄膜 MD, yield, 38 µ m, blow molded film |
% | ASTM D882 | |
TD,屈服,38 µm,吹塑薄膜 TD, yield, 38 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
g | ASTM D4272 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:38 µm,吹塑薄膜 MD: 38 µ m, blow molded film |
g | ASTM D1922 | |
TD:38 µm,吹塑薄膜 TD: 38 µ m, blow molded film |
g | ASTM D1922 | |
氧气传输速率 Oxygen transfer rate |
|||
23℃,38 µm,吹塑薄膜 23 ℃, 38 µ m, blow molded film |
cm³/m²/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
|||
38℃,38 µm,吹塑薄膜 38 ℃, 38 µ m, blow molded film |
g/m²/24 hr | ASTM F372 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
℃ | DSC | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,38.1 µm,吹塑薄膜 45 °, 38.1 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
38.1 µm,吹塑薄膜 38.1 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
NAS(38.1 µm) NAS(38.1 µm) 2 |
ASTM D1746 |
备注 |
---|
2 Blown Film |
【新闻资讯】查看全部
多国对一次性塑料产品的禁令将越来越严厉
2016-09-22 据《独立报》报道,法国已经通过了一项法律,要求逐步禁止使用一切塑料材质的一次性餐具,包括杯子、盘子、刀叉和匙等。今后,这些用品将必须由可堆肥材质或生物来源的材料制成。 作为法国政府Energy Transition for Green Growth法案的一部分,该禁令将于2020年正式生效。 现在,法国每年丢弃的塑料杯子就达到47.3亿个,被回收的只有其中微不足道的1%。这些塑料垃圾会最终沉积在海洋中,危害水生环境。而且,人们也越来越担心自己正在使用的塑料餐 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |