Lexan 221R树脂17.5 mfr,用于小型复杂零件。提高了阻燃性。内部模具释放。Lexan 221R树脂Lexan 221R是一种低粘度多用途等级,包含释放剂,以确保易于加工。该等级为UL94-V2,批准0.4 mm。 17.5 MFR, for small, intricate parts. Improved flame retardance. Internal mold release. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PC Polycarbonate
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级V-0; 防火阻燃等级V-2; 阻燃; 低粘度; 易加工; Excellent Processability,Low Viscosity,Flame Characteristics,V-2,V-0
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
特定体积 Specific volume |
0.835 | cm³/g | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
18 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.50 to 0.70 | % | 内部方法 |
吸水率 Water absorption rate |
ASTM D570 | ||
24hr 24hr |
0.15 | % | ASTM D570 |
平衡,23℃ Equilibrium, 23 ℃ |
% | ASTM D570 | |
平衡,100℃ Equilibrium, 100 ℃ |
% | ASTM D570 | |
耐候性 Weathering resistance |
UL 746C | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ |
J/m | ASTM D256 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
落锤冲击 Drop hammer impact |
|||
23℃ 23℃ |
J | ASTM D3029 | |
拉伸冲击强度 Tensile impact strength 4 |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 5 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~95℃ MD:-40~95℃ |
1/℃ | ASTM E831 | |
比热 specific heat |
J/kg/℃ | ASTM C351 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
3.2 mm,在空气中 3.2 mm in air |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.10 mm 1.10 mm |
UL 94 | ||
6.00 mm 6.00 mm |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
MPa | ASTM D638 | |
屈服 yield 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
屈服 yield 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 4 |
|||
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | ASTM D1044 | |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Tensile Bar |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*3 sp=62mm |
8 80*10*3 |
9 Type S |
10 120*10*4 mm |
11 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
中石化催化剂与西南院签署战略合作协议
2021-05-17 搜料网资讯: 5月11日,中国石化 催化剂 有限公司与西南化工研究设计院有限公司(以下简称西南院)在成都市召开合作会议并签署战略合作协议。 西南院党委书记、总经理陈健,副总 |
中石化催化剂与西南院签署战略合作协议 搜料网资讯:5月11日,中国石化催化剂有限公司与西南化工研究设计院有限公司(以下简称“西南院”)在成都市召开合作会议并签署战略合作协议。
西南院党委书记、总经理陈健,副总经理王键,副总经理兼催化剂事业部总经理郑珩及相关部门领导专家,催化剂公司董事、总经理、党委副书记焦阳,副总经理刘志坚及相关部门领导专家参加签约仪式。西南院副总经理郑珩主持会议。 会上,西南院变压吸附分离工程研究所总工程师张剑锋、催化剂事业部副总经理杜勇分别介绍《吸附分离技术在石化行业的研究开发和应用》和《西南院制氢催化剂和甲醇合成催化剂的研究开发和应用》两项课题,双方就合作事宜进行了交流协商。 西南院党委书记、总经理陈健表示,双方将以优势互补、合作共赢为原则,发挥协同创新优势,在科技创新平台建设、项目合作开发、科技成果转化与推广、技术升级等方面开展全方位合作,共同引领催化剂产业技术进步,壮大催化剂产业规模,提高经济与社会效益。 催化剂公司董事、总经理、党委副书记焦阳表示,此次战略协议的签署对催化剂公司扩大技术来源、推进高质量创新具有重要意义,相信双方将不断发挥各自优势,一致践行精诚合作、互利互惠的理念,为催化剂公司贯彻新发展理念、融入新发展格局,走稳走实高质量发展新征程提供强大助力。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。