牌号简介 About |
---|
PLURIS6301是一种采用球墨技术生产的Braskem四元共聚物。该等级具有独特的性能,例如与韧性相关的高刚度。除了良好的加工性能外,还显示出非常好的气泡稳定性和极低的凝胶含量。应用:冷冻袋,自动包装用高性能结构(共挤)。添加剂:防堵介质滑动介质加工助剂介质工艺:吹膜挤出 Pluris6301 is a Braskem Quatropolymer that shows unique properties, such as high stiffness associated with toughness. In addition to good processability, also shows a very good bubble stability and very low gel content. Applications: Frozen bags, high performance structures (coextrusion) for automatic packaging (FFS). Additive: Antiblocking medium Slip medium Processing Aid medium Process: Blown Film Extrusion |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.919 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.85 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
35.0 | MPa | ASTM D882 |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
45.0 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
1300 | % | ASTM D882 |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
弯曲模量 Bending modulus |
|||
1% 正割,TD,40 µm,吹塑薄膜 1% secant, TD, 40 µ m, blow molded film |
MPa | ASTM D790 | |
1% 正割,MD,40 µm,吹塑薄膜 1% secant, MD, 40 µ m, blow molded film |
MPa | ASTM D790 | |
落锤冲击 Drop hammer impact |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ASTM D1709 | |
撕裂强度 tear strength |
|||
TD,40 µm,吹塑薄膜 TD, 40 µ m, blow molded film |
g | ASTM D1922 | |
MD,40 µm,吹塑薄膜 MD, 40 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,40.0 µm,吹塑薄膜 60 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部
废旧农膜回收会宁县小有成效
2017-12-29 今年以来,会宁县坚持把废旧农膜回收利用作为推进节能减排、发展循环经济、促进生态文明建设的重要抓手,不断加大资金投入,强化政策扶持,大力组织开展废旧农膜污染防治、试验示范、资源调查等活动。并与回收加工企业签订《包片回收协议书》,明确各加工企业的回收区域,量化了回收目标任务。同时,积极引导回收企业提升产能规模,废旧农膜回收成效日渐凸显,基本形成了县有回收企业、乡镇有回收站、村有回收点,布局合理、方便群众交易的废旧农膜回收加工体系。 截至目前,该县已建成废旧塑料回收加工企业6家, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |