Polipom C250是一种聚甲醛(POM)共聚物材料,。 该产品在非洲和中东、拉丁美洲、欧洲或亚太地区有供货,。 ICORENE® N1007 is a premium copolymer of ethylene vinyl acetate specifically designed for the preparation of masterbatch. The powder form can achieve better colour developments or additive dispersion in a masterbatch than the pellet form. The vinyl acetate content is about 14 %. Maximum processing tem- perature 240°C. . |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.934 | g/cm³ | 内部方法 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
7.5 | g/10min | ASTM D1238 |
醋酸乙烯含量 Vinyl acetate content |
14.0 | wt% | 内部方法 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
61.0 | ℃ | ASTM D1525 |
熔融峰值温度 Melting peak temperature |
88.0 | ℃ | ASTM D3418 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Without Load |
【新闻资讯】查看全部
碳纤维及其复合资料的市场需求预测
2015-12-17 图1示出美国复合材料协会和A V K碳纤维复合材料研究所共同统计的全球2008-2020年CF的需求情况,图2示出全球2008-2020年C F R P的需求增长预测。由这2图可以看出,2015年起C F和C F R P的需求出现较快增长,5年间C F和C F R P各增长约91%和93%。 图3示出2008-2020年C F在汽车的消费变化及未来发展预测。不难看出2015年后的市场推动力主要是汽车领域。 据统计2012年C F在航空航天和国防领域的消费量约 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |