牌号简介 About |
---|
对于工业和消费类薄膜应用,具有优异的抗冲击性、高模量和低阻塞倾向,其处理和可兑换性符合美国FDA 21 CFR 177.1520(c)3.2a的要求。有关完整的详细信息,请参考法规。ELITE™ 5110G增强聚乙烯树脂是由陶氏塑料通过InSite技术生产的共聚物。它提供了一个独特的组合,高模量和良好的冲击强度,允许在袋应用向下测量。Elite 5110树脂具有优异的拉伸强度和撕裂性能。它符合美国食品和药物管理局条例21 CFR 177.1520(c)3.2A,使用时未经修改,并按照良好的制造规范进行加工。关于食品接触合规声明,请联系您最近的陶氏办公室。 For industrial and consumer film applications Excellent impact resistance High modulus and low blocking tendencies for handling and convertibility Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a. Consult the regulations for complete details. ELITE™ 5110G Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow Plastics. It offers a unique combination of high modulus and excellent impact strength, allowing for downgauging in bag applications. ELITE 5110 resin has excellent tensile strength and good tear properties. It complies U.S. FDA regulation 21 CFR 177.1520 (c) 3.2a when used unmodified and processed according to good manufacturing practices. Please contact your nearest Dow office regarding food contact compliance statements. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.926 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.85 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
51 | µm | |
膜刺穿强度 Membrane puncture strength |
|||
51 µm 51 µm |
6.91 | J | 内部方法 |
膜刺穿力 Membrane puncture force |
|||
51 µm 51 µm |
97.0 | N | 内部方法 |
割线模量 Secant modulus |
ASTM D882 | ||
2% 正割,MD:51 µm 2% secant, MD: 51 µ m |
MPa | ASTM D882 | |
2% 正割,TD:51 µm 2% secant, TD: 51 µ m |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ASTM D882 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ASTM D882 | |
MD,断裂,51 µm MD, fracture, 51 µ m |
MPa | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,51 µm MD, fracture, 51 µ m |
% | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
51 µm 51 µm |
g | ASTM D1709-B | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:51 µm MD:51 µm |
g | ASTM D1922 | |
TD:51 µm TD:51 µm |
g | ASTM D1922 | |
始封温度 Initial sealing temperature 2 |
|||
51 µm 51 µm 2 |
℃ | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.8 µm 45°,50.8 µm |
ASTM D2457 | ||
雾度 Haze |
|||
50.8 µm 50.8 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 实现 2 磅/英寸 (8.8 N/25.4 mm) 热封强度的温度。 J&B 自动热封和热粘性测试仪 0.5 S 保压,40 psi 压力,Instron 拉动速度 1.0 英寸/分。 |
【新闻资讯】查看全部
丰田新概念车运用Textreme碳纤资料
2016-04-19 Deep Orange 6是下一代丰田概念车的代号,由美国克莱蒙森大学(Clemson University)的学生开发研制,在上周的汽车业界活动上亮相。 这次活动即"SAE国际2016大会及展览",在美国底特律举办。这款丰田概念车的车门面板、后掀背车门、仪表板、保险杠和覆盖层等均采用了TeXtreme碳纤维材料。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |