牌号简介 About |
---|
超乙烯UE672是一系列韧性好、柔韧性好、澄清度好的EVA共聚树脂。典型应用包括层压和重型薄膜以及注塑和吹塑。 Ultrathene UE672 is a series of EVA copolymer resins with good toughness, flexibility and clarity. Typical applications include laminating and heavy duty films as well as injection and blow molding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.50 | g/10min | ASTM D1238 |
醋酸乙烯含量 Vinyl acetate content |
13.5 | wt% | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
38 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:38 µm,吹塑薄膜 1% secant, MD: 38 µ m, blow molded film |
90.3 | MPa | ASTM D882 |
1% 正割,TD:38 µm,吹塑薄膜 1% secant, TD: 38 µ m, blow molded film |
91.0 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,38 µm,吹塑薄膜 MD, yield, 38 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,38 µm,吹塑薄膜 TD, yield, 38 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,屈服,38 µm,吹塑薄膜 MD, yield, 38 µ m, blow molded film |
% | ASTM D882 | |
TD,屈服,38 µm,吹塑薄膜 TD, yield, 38 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
g | ASTM D4272 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:38 µm,吹塑薄膜 MD: 38 µ m, blow molded film |
g | ASTM D1922 | |
TD:38 µm,吹塑薄膜 TD: 38 µ m, blow molded film |
g | ASTM D1922 | |
氧气传输速率 Oxygen transfer rate |
|||
23℃,38 µm,吹塑薄膜 23 ℃, 38 µ m, blow molded film |
cm³/m²/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
|||
38℃,38 µm,吹塑薄膜 38 ℃, 38 µ m, blow molded film |
g/m²/24 hr | ASTM F372 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
℃ | DSC | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,38.1 µm,吹塑薄膜 45 °, 38.1 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
38.1 µm,吹塑薄膜 38.1 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
NAS(38.1 µm) NAS(38.1 µm) 2 |
ASTM D1746 |
备注 |
---|
2 Blown Film |
【新闻资讯】查看全部
美国陶氏化学计划未来五年将在华销售额提高5倍
2016-08-16 据报道,美国陶氏化学首席执行官利伟诚(Andrew Liveris)称,中国在食品安全和节能等领域的化学品需求,在较长一段时期内将有望增长,陶氏将与杜邦在发挥企业合并效果,以农业等领域为中心扩大业务。要在今后20年左右,将在华业务的销售额提高至5倍,达到200亿美元。 对于在华扩大业务,利伟诚认为陶氏的竞争对手是中国企业。他指出陶氏特别关注中国化工集团和中国石油化工集团等中国国有企业的动向。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |