牌号简介 About |
---|
超乙烯UE672是一系列韧性好、柔韧性好、澄清度好的EVA共聚树脂。典型应用包括层压和重型薄膜以及注塑和吹塑。 Ultrathene UE672 is a series of EVA copolymer resins with good toughness, flexibility and clarity. Typical applications include laminating and heavy duty films as well as injection and blow molding. |
产品描述 Product Description
厂家:荷兰利安德巴塞尔 LyondellBasell
类别:EVA EVA
用途:薄膜;层压板;吹塑成型应用;
加工条件:注射成型 Injection Molding
性能特点: 抗结块性; 共聚物; 透光性好; 食品接触; 韧性好; Good Clarity,Good flexibility,High anti-blocking,Food contact compliance,Copolymer
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.50 | g/10min | ASTM D1238 |
醋酸乙烯含量 Vinyl acetate content |
13.5 | wt% | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
38 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:38 µm,吹塑薄膜 1% secant, MD: 38 µ m, blow molded film |
90.3 | MPa | ASTM D882 |
1% 正割,TD:38 µm,吹塑薄膜 1% secant, TD: 38 µ m, blow molded film |
91.0 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,38 µm,吹塑薄膜 MD, yield, 38 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,38 µm,吹塑薄膜 TD, yield, 38 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,屈服,38 µm,吹塑薄膜 MD, yield, 38 µ m, blow molded film |
% | ASTM D882 | |
TD,屈服,38 µm,吹塑薄膜 TD, yield, 38 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
g | ASTM D4272 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:38 µm,吹塑薄膜 MD: 38 µ m, blow molded film |
g | ASTM D1922 | |
TD:38 µm,吹塑薄膜 TD: 38 µ m, blow molded film |
g | ASTM D1922 | |
氧气传输速率 Oxygen transfer rate |
|||
23℃,38 µm,吹塑薄膜 23 ℃, 38 µ m, blow molded film |
cm³/m²/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
|||
38℃,38 µm,吹塑薄膜 38 ℃, 38 µ m, blow molded film |
g/m²/24 hr | ASTM F372 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
℃ | DSC | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,38.1 µm,吹塑薄膜 45 °, 38.1 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
38.1 µm,吹塑薄膜 38.1 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
NAS(38.1 µm) NAS(38.1 µm) 2 |
ASTM D1746 |
备注 |
---|
2 Blown Film |
【新闻资讯】查看全部
美国陶氏化学计划未来五年将在华销售额提高5倍
2016-08-16 据报道,美国陶氏化学首席执行官利伟诚(Andrew Liveris)称,中国在食品安全和节能等领域的化学品需求,在较长一段时期内将有望增长,陶氏将与杜邦在发挥企业合并效果,以农业等领域为中心扩大业务。要在今后20年左右,将在华业务的销售额提高至5倍,达到200亿美元。 对于在华扩大业务,利伟诚认为陶氏的竞争对手是中国企业。他指出陶氏特别关注中国化工集团和中国石油化工集团等中国国有企业的动向。 |
美国陶氏化学计划未来五年将在华销售额提高5倍 据报道,美国陶氏有机化学CEO利伟诚(Andrew Liveris)称,中国在食品卫生安全和环保节能等行业的化工品要求,在很长一段阶段内将有希望提高,陶氏将与美国杜邦在充分发挥公司合并实际效果,以农牧业等行业为中心扩张业务。要在将来20年上下,将在华业务的销售总额提升至5倍,做到200亿美金。 针对在华扩张业务,利伟诚觉得陶氏的竞争者是中国公司。他强调陶氏特别关心中国化工集团和中国石油化工设备集团公司等中国国企的趋势。 来源于:阿思达克财经头条 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。