牌号简介 About |
---|
OC-5050是一种水透明、半柔性聚氨酯弹性体,适用于室温手工配料或真空辅助加工。无需使用汞、MOCA或TDI,室温固化即可获得优异的物理性能。OC-5050具有低粘度,使用具有优良耐紫外线性能的材料。 OC-5050 is a water clear, semi-flexible polyurethane elastomer formulated for room temperature hand-batch or vacuum assisted processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA,or TDI. OC-5050 has low viscosity and uses materials that have excellent U.V. resistant qualities. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
基体树脂 Matrix resin |
1.07 | g/cm³ | |
固化处理 Curing treatment |
1.07 | g/cm³ | |
Hardener Hardener |
1.10 | g/cm³ | |
收缩率 Shrinkage rate |
|||
MD MD |
0.10 到 0.30 | % | ASTM D2566 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
树脂 resin |
按重量计算的混合比: 50 按容量计算的混合比: 51 | ||
硬化法 Hardening method |
|||
脱模时间 stripping time |
min | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
粘度 viscosity |
|||
25℃ 25℃ 2 |
Pa·s | ||
25℃ 25℃ 3 |
Pa·s | ||
25℃ 25℃ 4 |
Pa·s | ||
固化时间 Curing time 5 |
hr | ||
胶凝时间 Gelation time |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
撕裂强度 tear strength |
kN/m | ASTM D624 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Hardener |
3 Mixed |
4 Resin |
5 24 hours at 77°F + 16 hours at 150°F |
【新闻资讯】查看全部
人形机器人时代即将到来,金发科技的特种工程塑料有望实现爆炸式增
2022-08-23 最近,在小米的秋季发布会上,小米集团创始人雷军首次发布了小米的第一个全尺寸仿人仿生机器人CyberOne。不久前,马斯克还宣布,他将在9月份推出特斯拉的机器人人Optimus。人形机器 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |