牌号简介 About |
---|
适用于注塑、挤出、压延等工序。注塑周期短,生产效率高。稳定熔体易于挤出生产。耐水解,低温性能好,加工窗口宽。挤出吹塑,平模铸造薄膜,注射标签轮和电缆护套 Utomer Polyether type TPU which can be applied to Injection, Extrusion and Calendering. Molding cycle is short and efficient for Injection production. The stability melt is easy for Extrusion production. Hydrolysis resistance, low temperature performance with a wide processing window. Extrusion Blown, Flat Die Cast Film, Injection Tag Wheel and Cable Jacketing |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.12 | g/cm³ | ASTM D792 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
100% 应变 100% strain |
12.0 | MPa | ASTM D412 |
300% 应变 300% strain |
28.0 | MPa | ASTM D412 |
拉伸强度 tensile strength |
40.0 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
450 | % | ASTM D412 |
撕裂强度 tear strength |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
ASTM D395B | ||
23℃,70 hr 23℃,70 hr |
% | ASTM D395B | |
70℃,24 hr 70℃,24 hr |
% | ASTM D395B | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
℃ | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
磨损量 Wear amount |
mm³ | DIN 53516 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
一季度中国橡塑制品业利润438亿元 同比增长8.8%
2017-05-02 据国家统计局最新统计显示,一季度中国规模以上工业企业实现主营业务收入27.8万亿元人民币(下同),同比增长14.0%;实现利润总额17043亿元,同比增长28.3%,增速比1-2月份回落3.2个百分点。 发生主营业务成本23.7万亿元,增长13.8%;主营业务收入利润率为6.13%,同比提高0.68个百分点。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |