牌号简介 About |
---|
Adsyl 7416 XCP是一种高级聚烯烃,专门设计用于共挤薄膜应用中的密封层。该等级具有低密封启动温度和良好的光学性能。不含防滑或防堵添加剂。 Adsyl 7416 XCP is an advanced polyolefin selected by customers for use as a sealing layer in coextruded film applications. This grade features a low seal initiation temperature and good optics. It does not contain slip or anti-block additives. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
7.5 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲模量 Bending modulus |
600 | MPa | ISO 178 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
拉伸模量 Tensile modulus |
ISO 527-3/25 | ||
MD,50 µm MD,50 µm |
290 | MPa | ISO 527-3/25 |
TD,50 µm,铸造薄膜 TD, 50 µ m, cast thin film |
MPa | ISO 527-3/25 | |
拉伸强度 tensile strength |
ISO 527-3/500 | ||
屈服 yield |
MPa | ISO 527-2 | |
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
拉伸强度 tensile strength |
ISO 527-3/500 | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
拉伸应变 Tensile strain |
ISO 527-3/500 | ||
屈服 yield |
% | ISO 527-2 | |
MD,断裂,50 µm,铸造薄膜 MD, fracture, 50 µ m, cast thin film |
% | ISO 527-3/500 | |
TD,断裂,50 µm,铸造薄膜 TD, fracture, 50 µ m, cast thin film |
% | ISO 527-3/500 | |
拉伸应变 Tensile strain |
ISO 527-3/500 | ||
MD,屈服,50 µm,铸造薄膜 MD, yield, 50 µ m, cast thin film |
% | ISO 527-3/500 | |
TD,屈服,50 µm,铸造薄膜 TD, yield, 50 µ m, cast thin film |
% | ISO 527-3/500 | |
始封温度 Initial sealing temperature |
℃ | Internal Method | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.0 µm,铸造薄膜 45 °, 50.0 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,铸造薄膜 50 µ m, cast thin film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
塑料的使用范畴
2018-08-22 自上世纪90年代中期开始,瓶装饮料使用铝塑组合盖开启力试验仪,从而将塑料防盗盖推到了饮料包装的前台。此后,我国国内有实力的包装企业和饮料生产商纷纷引进国外设备,开始了塑料防盗盖的大规模生产和应用。如今,既轻薄又易于开启的塑料瓶盖用于饮料包装不仅方便了消费者,同时也加快了饮料业的发展。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |