牌号简介 About |
---|
Ultramid® HPN 9350 HS是一种柔性、热稳定、冲击改性的PA6挤出级树脂。它具有良好的柔韧性、韧性和耐磨性等性能平衡。添加热稳定剂系统可延长其在高温下的性能保持期。耐化学性对油脂、油和碳氢化合物非常好。应用Ultramid® HPN 9350 HS通常推荐用于汽车发动机罩下管道、挡风玻璃清洗器管道、电缆护套和其他管道。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.06 | g/cm³ | ASTM D792 |
密度 Density |
1.06 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
1.3 | % | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
6.8 | % | ISO 62 |
饱和 saturated |
6.8 | % | ASTM D570 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,50% RH Balance, 50% RH |
% | ASTM D570 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
ISO 179 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
落下冲击阻力 Falling impact resistance |
|||
23℃ 23℃ |
J | Internal Method | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
23℃ 23℃ |
MPa | ISO 178 | |
-40℃ -40℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ASTM D790 | |
65℃ 65℃ |
MPa | ASTM D790 | |
90℃ 90℃ |
MPa | ASTM D790 | |
121℃ 121℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
23℃ 23℃ |
MPa | ISO 178 | |
-40℃ -40℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ASTM D790 | |
65℃ 65℃ |
MPa | ASTM D790 | |
90℃ 90℃ |
MPa | ASTM D790 | |
121℃ 121℃ |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部 ![]()
突发!杜邦宣布终止对电子材料制造商罗杰斯的收购
2022-11-03 扫描上图二维码,可以免费下载 搜料 APP 11月2日,化工材料巨头杜邦宣布,由于未能及时获得监管机构的批准,宣布终止其与罗杰斯的收购交易。 根据声明,杜邦公司需向罗杰斯支付了 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |