牌号简介 About |
---|
由IEPL利用加拿大杜邦的“sclairtech”溶液聚合工艺生产的NGH045IU高密度聚乙烯树脂(现为Nova Chemicals)提供具有窄分子量分布的中等分子量材料,以展示其改进的加工性能、优异的冲击强度、抗应力开裂性和紫外线稳定性。r用最小翘曲度注射成型零件,如容器、尘箱、桶、工业零件、矿泉水瓶盖。 NGH045IU High Density Polyethylene Resin manufactured by IEPL using "SCLAIRTECH" solution polymerisation process of DU Pont, Canada (Now Nova Chemicals) offers medium molecular weight material with narrow molecular weight distribution to exhibit improved processability, excellent impact strength, stress crack resistance and UV stability for outdoor use at minimum warpage to injection moulded parts like containers, dust bin, pails, Industrial Parts, bottle caps for mineral water. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.956 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
4.5 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
70 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
128 | ℃ | ASTM D1525 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
69 | ASTM D2240 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
1~11月中国塑料制品总产量6989万吨 同比增长3.9%
2016-12-20 据国家统计局最新统计显示,2016年1-11月份,中国规模以上工业增加值同比增长6.0%。 11月份,中国规模以上工业增加值同比实际增长6.2%,较10月份加快0.1个百分点。从环比看,11月份规模以上工业增加值比上月增长0.51%。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |