牌号简介 About |
---|
Hostalen CRP 100 black (XL)是一种高密度聚乙烯(HDPE),黑色类似RAL 9004,具有较高的熔融粘度和较高的零粘度。典型应用:超大型和厚壁管道的挤压,以避免下垂。该产品被归类为PE100,具有优异的抗应力开裂性能(ESCR),并具有很好的长期静液强度。它不适用于医疗和制药应用。 Hostalen CRP 100 black (XL) is a high density polyethylene (HDPE), black colored similar RAL 9004 with high melt viscosity particularly higher zero viscosity than standard compounds. Typical application: Extrusion of extra large and thick walled pipes to avoid the sagging of the melt and to maintain uniform wall thickness. The product is classified as PE 100 and provides good stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.959 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
0.23 | g/10min | ISO 1133 |
190℃,21.6kg 190℃,21.6kg |
6.4 | g/10min | ISO 1133 |
炭黑含量 Carbon black content |
2.3 | % | ISO 6964 |
全切口蠕变试验 Full incision creep test 2 |
|||
80℃ 80℃ 2 |
> 1.4 | month | ISO 16770 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
氧感应时间 Oxygen sensing time |
|||
210℃ 210℃ |
min | ISO 11357-6 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
MRS Classification MRS Classification |
MPa | ISO TR 9080 | |
Odor Threshold Odor Threshold |
EN 1622/EN 1420 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,3 秒 Shore D, 3 seconds |
ISO 868 | ||
拉伸模量 Tensile modulus |
|||
正割,23℃ Secant, 23 ℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | EN 638 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
拉伸蠕变模量 Tensile creep modulus 3 |
ISO 899-1 | ||
1 hr 1 hr |
MPa | ISO 899-1 | |
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲蠕变模量 Bending creep modulus 4 |
DIN 19537-2 | ||
1 min 1 min |
GPa | DIN 19537-2 | |
2000 hr 2000 hr |
GPa | DIN 19537-2 | |
24 hr 24 hr |
GPa | DIN 19537-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 4.0 MPa, 2% Arkopal N 100 |
3 2.0 MPa load |
4 4 point loading method |
【新闻资讯】查看全部
乐天化学使用巴斯夫稳定剂为新冠疫苗接种注射器提供高清晰度医用聚
2021-08-19 搜料网资讯: 韩国一家大型化工公司乐天化学已经使用巴斯夫的Irgastab(一种不褪色的加工稳定剂)生产了医疗应用所需的PP。巴斯夫的新闻稿称,随着新冠疫苗在全世界的推广,对PP制 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |