牌号简介 About |
---|
HI650是一种高抗冲击等级的注射用聚苯乙烯树脂,具有良好的抗冲击性和流动性。建议用于电器(空调部件、电视)、家用产品、卫生洁具和玩具。符合食品接触法规要求 HI650 is a high impact grade of polystyrene resin for injection molding with good impact resistance and easy flow. It is recommended for electrical appliances (air conditioning parts, TV), household products, sanitary ware, and toys. It also meets the requirement of food contact regulation |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
8.0 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,5.84mm 23℃,5.84mm |
110 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,6.35 mm 1.8 MPa, unannealed, 6.35 mm |
90.0 | ℃ | ASTM D648 |
维卡软化温度 Vicat Softening Temp |
96.0 | ℃ | ASTM D1525 |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
HB | UL 94 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
L 级,23℃,6.35 mm L-grade, 23 ℃, 6.35 mm |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D790 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
塑料制品包装对化工行业既是机遇又是应战
2017-10-13 塑料制品包装行业正朝着功能化、绿色化、减量化发展,对化工行业既是机遇又是挑战。配套化工产品若想在这一领域开辟新的市场份额,就需要加大相关材料的开发和推广力度。 作为石化产业最直接的下游行业之一,塑料包装的升级和技术进步高度依赖化工产品的支撑。同时,随着百姓生活水平的提高以及消费领域个性化需求日益增长,塑料包装对化工产品也提出了越来越高的要求 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |