牌号简介 About |
---|
D/W 212是一种用纯聚四氟乙烯(PTFE)刮削而成的薄膜,该薄膜一面用萘钠蚀刻。这种表面处理可以使聚四氟乙烯(通常表现出很差的粘附力)与其他材料结合。钠蚀聚四氟乙烯的主要应用包括与弹性体粘合以生产层压隔膜,以及在聚四氟乙烯压敏带生产中应用压敏粘合剂。在上述所有应用中,层压或粘合应用通常通过特定于所应用材料的底漆完成。 D/W 212 is a film , skived from virgin PTFE, that has been etched on one side with sodium naphthalene. This surface treatment allows PTFE, which normally exhibits very poor adhesion, to be bonded to other materials. The major applications for sodium etched PTFE involve bonding to elastomers to produce laminated diaphragms, as well as the application of pressure sensitive adhesives in the production of PTFE pressure sensitive tapes. In all the above applications, the lamination or adhesive application is usually accomplished with a primer that is specific to the material being applied. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Thickness Thickness |
50.8 到 1020 | nm | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
MD,屈服 MD, yield |
27.6 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
MD,断裂 MD, fracture |
300 | % | ASTM D882 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
连续使用温度 Continuous use temperature |
260 | ℃ | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Core ID Core ID |
7.62 | cm | |
Maximum Roll OD Maximum Roll OD |
mm | ||
Width Width |
mm |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
陶氏CEO利伟诚:合理的环境监管可以促进投资和失业
2017-03-21 3月18日-20日,由国务院发展研究中心主办的“中国发展高层论坛2017年会”在京举行。陶氏化学公司董事长、首席执行官利伟诚在论坛上表示,通过合理的监管,可以保护投资、促进投资和就业,在保护环境的同时保护经济的增长。 利伟诚表示,在世界快速发展的今天,长期的环境问题给人们提出了新的挑战,一个国家必须在保证经济增长的同时保证环境的可持续性。利用科技和创新解决发展中出现的环境问题,可以造福于中国,造福于全人类。科技的力量、合作的潜力,帮助社会、帮助企业客户能够快速的发展。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |