牌号简介 About |
---|
PRL PEI-GP1-TFE5是一种聚醚酰亚胺(PEI)产品,。 它可以通过注射成型进行加工,在北美洲有供货。 特性包括: 通过 ROHS 认证 Flame Retardant 润滑 耐热 PRL PEI-GP1-TFE5 is a Polyether Imide (PEI) product. It can be processed by injection molding and is available in North America. Characteristics include: RoHS Compliant Flame Retardant Heat Resistant Lubricated |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
1.27 | g/cm³ | ASTM D792 |
-- -- |
1.27 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
337℃,6.60kg 337℃,6.60kg |
5.0 to 30 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
TD:3.2 mm TD:3.2 mm |
0.50 to 0.70 | % | ASTM D955 |
MD:3.2 mm MD:3.2 mm |
0.50 to 0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃,3.2mm -30℃,3.2mm |
J/m | ASTM D256 | |
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃,3.2 mm 23℃,3.2 mm |
J/m | ASTM D4812 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
落锤冲击 Drop hammer impact |
|||
3.2 mm 3.2 mm |
J | ASTM D3029 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 3 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~150℃ TD:23~150℃ |
1/℃ | ISO 11359-2 | |
TD:-20:150℃ TD:-20:150℃ |
1/℃ | ASTM E831 | |
MD:23~150℃ MD:23~150℃ |
1/℃ | ISO 11359-2 | |
MD:-20~150℃ MD:-20~150℃ |
1/℃ | ASTM E831 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1 | |
3.18 mm 3.18 mm |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
断裂,3.18 mm Fracture, 3.18 mm |
MPa | ASTM D638 | |
屈服,3.17 mm Yield, 3.17 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,3.18 mm Fracture, 3.18 mm |
% | ASTM D638 | |
屈服,3.18 mm Yield, 3.18 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
3.17 mm 3.17 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength 2 |
MPa | ISO 178 | |
3.18 mm 3.18 mm |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Yield |
3 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
赢创扩大奥地利气体分离膜投资规模
2021-04-05 搜料网资讯: 德国埃森赢创工业集团,领先的特殊化学品制造商,正着手扩大其在奥地利的薄膜业务。 赢创扩大奥地利气体分离膜投资规模 因此,该公司将继续奥地利工厂的生产规模 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |