牌号简介 About |
---|
NorylGTX989是一种导电和高热材料,特别是专为在线和在线喷漆的车身板和挡泥板而设计。这种材料结合了冲击性能和导电性,以独特的方式进行静电喷涂。 NORYL GTX989 is a conductive and high heat material, especially designed for in- and on-line painted bodypanels and fenders in particular. This material combines impact performance with conductivity for electro-static painting in an unique way. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | ASTM D792 , ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
280℃,5.0kg 280℃,5.0kg |
16 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
280℃,5 kg 280℃,5 kg |
19.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
1.2 到 1.6 | % | 内部方法 |
吸水率 Water absorption rate |
ISO 62 | ||
饱和,23℃ Saturation, 23 ℃ |
4.2 | % | ISO 62 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 2 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
-- -- 5 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 5 , 6 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 8 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 8 |
kJ/m² | ISO 180-1A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,100 mm跨距 0.45 MPa, unannealed, 100 mm span 9 |
℃ | ISO 75-2/Be | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ASTM D1525 10 , ISO 306/B50 10 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~60℃ MD:-40~60℃ |
1/℃ | ASTM E831 | |
MD:23~60℃ MD:23~60℃ |
1/℃ | ISO 11359-2 | |
TD:-40~60℃ TD:-40~60℃ |
1/℃ | ASTM E831 | |
TD:23~60℃ TD:23~60℃ |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | 内部方法 |
备注 |
---|
2 50 mm/min |
3 类型 1, 50 mm/min |
4 1.3 mm/min |
5 2.0 mm/min |
6 Yield |
7 80*10*4 sp=62mm |
8 80*10*4 |
9 120*10*4 mm |
10 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
2017年环保严查关停的上千家废塑料厂家
2017-12-25 自今年2月起,一场环境整治风暴吹遍全国各地,停产!刑拘!问责!这半年来,到底有多少家废塑料厂家被关停了?看看下面这些触目惊心的数据! 2-3月:山东沙河镇1700多家废塑料工厂 对涉塑业户集中的沙河镇1700多户塑料加工户“清设备、清原料、清产品”。有着30多年历史的塑料颗粒加工县,曾是全国再生塑料价格风向标。 3月10日至6月:福建郊尾镇将全部退出废塑料行业 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |