牌号简介 About |
---|
说明:EPOCAST1629-A/B环氧树脂复合材料是一种米黄色、自熄、超低密度的蜂窝结构边缘加固系统。它可以被挤出或用油灰刀蔓延,并抵抗在垂直表面上的坍塌。EPOCAST1629-A/B环氧树脂复合砂和机器固化后容易。它是一种不含PBDE的材料,可替代EPOCAST87005A/B-80环氧树脂句法、EPOCAST87005A/B-60环氧树脂句法、EPOCAST87269A/B环氧树脂句法、EPOCAST87005A/B-61环氧树脂句法和EPOCAST87005A/BE-60环氧树脂句法。 DESCRIPTION: Epocast® 1629-A/B epoxy syntactic is a beige-tan, self-extinguishing, ultra-low density system for edge reinforcing of honeycomb structures. It can be extruded or spread with a putty knife and resists slumping on vertical surfaces. Epocast® 1629-A/B epoxy syntactic sands and machines easily when cured. It is a non-PBDE containing material and can be used as a replacement for Epocast® 87005 A/B-80 epoxy syntactic, Epocast® 87005 A/B-60 epoxy syntactic, Epocast® 87269 A/B epoxy syntactic, Epocast® 87005 A/B-61 epoxy syntactic, and Epocast® 87005 A/BE- 60 epoxy syntactic. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
ASTM D1622 | ||
-- -- 2 |
0.420 | g/cm³ | ASTM D1622 |
-- -- 3 |
0.480 | g/cm³ | ASTM D1622 |
-- -- 4 |
0.520 | g/cm³ | ASTM D1622 |
粘度 viscosity |
ASTM D2196 | ||
-- -- 4 |
Paste | ASTM D2196 | |
-- -- 3 |
Paste | ASTM D2196 | |
-- -- 2 |
ASTM D2196 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
|||
25℃ 25℃ |
MPa | ASTM D695 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 5 |
|||
烧伤长度 Burn length |
cm | ||
自熄 Self extinguishing |
sec | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
胶凝时间 Gelation time |
|||
75 gms,25℃ 75 gms,25℃ |
hr | ASTM D2471 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
25℃ 25℃ |
day | ||
Tensile Lap Shear(etched al/al,25℃) Tensile Lap Shear(etched al/al,25℃) |
MPa | ASTM D1002 | |
体重增量 Weight gain 6 |
ASTM D543 | ||
Distilled water:25℃ Distilled water:25℃ |
% | ASTM D543 | |
Mil-M-5606,hydraulic fluid:25℃ Mil-M-5606,hydraulic fluid:25℃ |
% | ASTM D543 | |
Mil-S-3136,Type III test fluid:25℃ Mil-S-3136,Type III test fluid:25℃ |
% | ASTM D543 | |
Skydrol 500-A:25℃ Skydrol 500-A:25℃ |
% | ASTM D543 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Hardener |
3 System |
4 Resin |
5 12-second vertical |
6 on immersion - 24 hrs |
【新闻资讯】查看全部
生物降解材料获新进展 可承受60℃的PLA杯
2020-12-30 搜料网资讯: 美国阿克伦大学(University of Akron)高分子科学与聚合物工程学院王世清教授在可持续性的生物塑料方面取得重要进 展。 王世清教授及其团队一直致力于研究将脆性聚合物 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |