牌号简介 About |
---|
BaydUR 646是一种用于反应注射成型(RIM)工艺的硬质聚氨酯结构发泡体系。该系统作为两种反应性液体成分提供:组分A是聚合物二苯甲烷二异氰酸酯(PMDI),组分B是不含CFC-或HCFC发泡添加剂的配方多元醇系统。BaydUR 646系统用于生产复合材料的泡沫芯,例如滑水板、尾板、雪板以及运输和海洋市场的各种部件。与任何产品一样,在给定应用中使用Baydur 646系统必须由用户提前进行测试(包括现场测试等),以确定适用性。 Baydur 646 is a rigid polyurethane structural foam system used in the reaction injection molding (RIM) process. The system is supplied as two reactive liquid components: Component A is a polymeric diphenylmethane diisocyanate (PMDI), and Component B is a formulated polyol system containing no CFC- or HCFC-blowing additives. The Baydur 646 system is used to produce foam cores for composite applications, such as water skis, wake boards, snow boards, and various components for the transportation and marine markets. As with any product, use of the Baydur 646 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
产品描述 Product Description
厂家:德国科思创 Covestro
类别:PUR+MDI PUR+MDI
用途:汽车领域的应用;结构泡沫;体育用品;船舶应用;
加工条件:反应注射成型 (RIM)
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.399 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:6.35 mm MD:6.35 mm |
0.30 到 0.50 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
内部方法 | ||
-- -- 2 |
7.4 | kJ/m² | 内部方法 |
-- -- 3 |
8.0 | kJ/m² | 内部方法 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
部件 A Component A |
按重量计算的混合比: 110 | ||
部件 B Component B |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 D,6.35 mm Shaw D, 6.35 mm |
ASTM D2240 | ||
邵氏 D,12.70 mm Shore D, 12.70 mm |
ASTM D2240 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
断裂,6.35 mm Fracture, 6.35 mm |
MPa | ASTM D638 | |
断裂,12.70 mm Fracture, 12.70 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
断裂,6.35 mm Fracture, 6.35 mm |
% | ASTM D638 | |
断裂,12.70 mm Fracture, 12.70 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
6.35 mm 6.35 mm |
MPa | ASTM D790 | |
12.70 mm 12.70 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
6.35 mm 6.35 mm |
MPa | ASTM D790 | |
12.70 mm 12.70 mm |
MPa | ASTM D790 | |
压缩强度 compressive strength |
ASTM D695 | ||
6.35 mm 6.35 mm |
MPa | ASTM D695 | |
12.7 mm 12.7 mm |
MPa | ASTM D695 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.5 |
3 0.25 in |
【新闻资讯】查看全部
2018上半年中国聚乙烯出口量约为718.8万吨
2018-07-23 据统计,2018上半年中国聚乙烯进口量约为718.8万吨,同比去年上半年增长27.64%,年初,禁塑令与环保税相继实行,不符合环保要求的企业遭到整改与停产。再生PE产量大幅下降,加之五月国内石化装置集中检修,导致上半年聚乙烯进口量大幅增长。 |
2018上半年中国聚乙烯出口量约为718.8万吨 据统计,2018上半年中国聚乙烯进口量约为718.8万吨,同比去年上半年增长27.64%,年初,禁塑令与环保税相继实行,不符合环保要求的企业遭到整改与停产。再生PE产量大幅下降,加之五月国内石化装置集中检修,导致上半年聚乙烯进口量大幅增长。 占比情况来看,进口低压占比48.63%,进口线性占比29.35%,高压进口量占比最小,其进口量占PE进口总量的21.10%。 来源:买化塑研究院 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。