牌号简介 About |
---|
40%gf钢筋用于电机绝缘体的材料 Infino GP-5400G is a Polybutylene Terephthalate (PBT) product filled with 40% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Wire & Cable. Primary characteristic: flame rated. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
- - |
1.61 | g/cm³ | ISO 1183 |
|
1.61 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,2.16kg 250℃,2.16kg |
10 | g/10min | ISO 1133 |
250℃,2.16kg 250℃,2.16kg |
10 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
TD:3.2 mm TD:3.2 mm |
0.54 to 0.65 | % | ASTM D955 |
MD:3.2 mm MD:3.2 mm |
% | ASTM D955 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 5 |
|||
23℃ 23℃ 5 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃ 23℃ 5 |
kJ/m² | ISO 180-1A | |
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
23℃,6.4mm 23℃,6.4mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火,4.0 mm 1.8 MPa, annealed, 4.0 mm |
℃ | ISO 75-2/A | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ISO 75-2/A | |
0.45 MPa,退火,4.0 mm 0.45 MPa, annealed, 4.0 mm |
℃ | ISO 75-2/B | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,4.0 mm 0.45 MPa, unannealed, 4.0 mm |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.70 mm 1.70 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 2 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus 4 |
MPa | ISO 178 | |
弯曲强度 bending strength 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
MPa | ISO 178 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
R 级 R-level |
ISO 2039-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 0.11 in/min |
4 0.079 in/min |
5 Thickness: 4mm |
【新闻资讯】查看全部
克服塑料熔体在模腔内不规则脉冲活动的办法
2018-03-16 熔体注入型腔后先在模具腔壁上形成一层薄的表壳,当这层表壳在充模过程中受到后续熔料的挤压时,就会导致熔体破裂。 一旦很薄的表壳被撕破或发生移动,塑件表面即产生搓痕或皱纹。例如,在熔体指数较小的低密度聚乙烯塑件上,其表面径常可以看到明暗交替的条形区域,其产生的部位一般离浇口有一定距离,并遍布整个表面,尤其是薄壁塑件最容易产生这类故障,这主要是由于熔料在充填小熔腔尚未结束前受到较大的压力,导致熔体破裂,形成表面缺陷。 通常,减慢熔料在充模过程中的冷却速度和表壳层的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |