牌号简介 About |
---|
由IEPL利用加拿大杜邦的“sclairtech”溶液聚合工艺生产的NGH200ig高密度聚乙烯树脂(现为Nova Chemicals)提供分子量分布非常窄的中等分子量材料,为G等注塑件提供优异的机械性能、高光泽和表面光洁度。一般家庭用品、玩具、容器、帽子、盖子、小桶等。 NGH200IG High Density Polyethylene Resin manufactured by IEPL using "SCLAIRTECH" solution polymerisation process of DU Pont, Canada (Now Nova Chemicals) offers medium molecular weight material with very narrow molecular weight distribution to impart excellent mechanical properties, high gloss and surface finishing to injection moulded parts like general housewares, toys, containers, caps, lids, small pails, etc. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.958 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
19 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
88 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
126 | ℃ | ASTM D1525 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
69 | ASTM D2240 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
巴陵石化橡胶部优化热塑性弹性体SEPS消费运转
2018-11-27 巴陵石化橡胶部优化热塑性弹性体SEPS生产运行,日产量由20吨增至40吨,质量明显提升,受到用户好评。 去年8月31日,巴陵石化橡胶部建成投产国内首套具有自主知识产权的年产2万吨热塑性弹性体SEPS(氢化苯乙烯/异戊二烯共聚物)工业化装置。在国外技术封锁、国内没有经验可借鉴的情形下,该部强化技术创新,持续优化生产配方、工艺流程和操作,探索提质增产经验。 据了解,该部目前生产的SEPS主要有两类,一类应用于光纤光缆油脂油膏,另一类用于弹性体新材料。SIS车间主 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |