| 牌号简介 About |
|---|
| Alathon® L5008是一种双峰、高分子量、高密度聚乙烯树脂，具有优良的加工性能。L5008是客户为要求压力管道应用而选择的。当L5008与Equistar认可的黑色在正确的负载下结合时，该化合物符合以下标准：塑料管道协会（PPI）PE 4608/PPI TR-3塑料管道协会（PPI）PE 3408/PPI TR-4 PE80/ISO 9080&ISO 12162 ASTM D3350电池分类PE445564C化学电阻/ASTM D2513 NSF标准14 A饮用水管道和配件的ND标准61“地热”热泵系统的PE管道和配件的NSF标准358-1 Alathon L5008 is a bimodal, high molecular weight, high density polyethylene resin with excellent processing characteristics. L5008 is selected by customers for demanding pressure pipe applications. When combined with an approved color or black masterbatch at the correct use level, L5008 may meet the following standards or requirements (see Technical Data Sheet for limitations and more information): ASTM D3350 Cell Classifications: PE445564C, PE445564E, PE445565C, PE445565E NSF Standard 14 and Standard 61 for Potable Water Pipe and Fittings NSF Standard 358-1 for PE Pipe and Fittings for "Geothermal" Heat Pump Systems PE80 per ISO 9080 & ISO 12162 Plastics Pipe Institute (PPI) PE 3408 and PE4608 per PPI TR-3 |
产品描述 Product Description
用途：配件;管道系统;
加工条件：挤出 Extrusion
性能特点： 共聚物; 高分子量; 双峰分子量分布; 易加工; Excellent Processability,High molecular weight,Copolymer,Bimodal molecular weight distribution
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.949 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
|
190℃，2.16kg 190℃，2.16kg |
0.070 | g/10min | ASTM D1238 |
|
190℃，21.6kg 190℃，21.6kg |
16 | g/10min | ASTM D1238 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
34.3 | MPa | ASTM D638 |
|
屈服 yield |
24.4 | MPa | ASTM D638 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
2% 正割 2% secant |
MPa | ASTM D790 | |
|
流体静力学设计基础 Fundamentals of Hydrostatic Design |
ASTM D2837 | ||
|
23℃ 23℃ |
MPa | ASTM D2837 | |
|
60℃ 60℃ |
MPa | ASTM D2837 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
DSC Induction Temperature DSC Induction Temperature |
℃ | ASTM D3350 | |
|
裂纹缓慢扩展 PENT Slow crack propagation PENT 2 |
|||
|
80℃ 80℃ 2 |
hr | ASTM F1473 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2.4 MPa |
|
【新闻资讯】查看全部
2018-2023年中国塑料制操行业市场前景剖析
2018-05-02 近年来，在“以塑代钢”的市场大环境下，政策的倾斜为塑料制品行业带来了良好的前景，中国的塑料制品产量环比去年同期增加明显。随着生活水平逐年提高，人们对塑料制品的环保要求也逐步提高，绿色低碳成为该行业共识，只有不断提高塑料制品的品质，拓宽其用途，向高端市场进军，才能迎来更多的发展机遇。 据中商产业研究院发布的《2018-2023年中国塑料制品行业市场前景及投资机会研究报告》数据统计显示，2017年中国塑料制品累计产量为7515.5万吨，累计增长3.4%。据中商产业研究院数据预测 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付