牌号简介 About |
---|
说明:FH35树脂是一种高密度聚乙烯,丁烯-1共聚物,采用溶液法生产,用于平模挤出薄膜,具有良好的机械性能。它含有抗氧化剂添加剂。用途:尿布、卫生巾等。 FH35 resin is a High Density Polyethylene that is designed for flat die film extrusion and shows good mechanical properties. Applications: Diapers, sanitary napkins and other specialties. Process: Cast Film Extrusion |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.942 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
4.9 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
20.0 | MPa | ASTM D882 |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
30.0 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
430 | % | ASTM D882 |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
弯曲模量 Bending modulus |
|||
1% 正割,TD,25 µm,吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
MPa | ASTM D790 | |
1% 正割,MD,25 µm,吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
MPa | ASTM D790 | |
撕裂强度 tear strength |
|||
TD,25 µm,吹塑薄膜 TD, 25 µ m, blow molded film |
g | ASTM D1922 | |
MD,25 µm,吹塑薄膜 MD, 25 µ m, blow molded film |
g | ASTM D1922 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
拓斯达智能设备总部基地项目一期正式开工建设
2022-03-03 近日, 拓斯达智能设备总部基地项目一期正式开工建设 。该项目是拓斯达继江苏拓斯达(吴中)项目、松山湖拓斯达智能制造综合服务示范项目后又一重大项目。项目建成投产后,预 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |