牌号简介 About |
---|
Alathon® L5906是一种具有广泛双峰分子量分布的高分子量高密度聚乙烯均聚物。这种树脂具有极好的刚度、很高的拉伸强度和低的凝胶。L5906由客户选择,用于胶带和纸替换应用,以及其他需要硬度和韧性的单层和多层薄膜。 Alathon L5906 is a high molecular weight high density polyethylene homopolymer with a broad bimodal molecular weight distribution. This resin exhibits excellent stiffness, very high tensile strength, and low gels. L5906 is selected by customers for use in draw tapes and paper replacement applications as well as other mono- and multi-layer films requiring both stiffness and toughness. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.960 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.075 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
割线模量 Secant modulus |
|||
TD,20 µm TD,20 µm |
1300 | MPa | ASTM D882 |
MD,20 µm MD,20 µm |
1240 | MPa | ASTM D882 |
拉伸强度 tensile strength |
|||
TD,断裂,20 µm TD, fracture, 20 µ m |
MPa | ASTM D882 | |
TD,屈服,20 µm TD, yield, 20 µ m |
MPa | ASTM D882 | |
MD,断裂,20 µm MD, fracture, 20 µ m |
MPa | ASTM D882 | |
MD,屈服,20 µm MD, yield, 20 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂,20 µm TD, fracture, 20 µ m |
% | ASTM D882 | |
MD,断裂,20 µm MD, fracture, 20 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 2 |
|||
20 µm 20 µm 2 |
g | ASTM D1709 | |
撕裂强度 tear strength |
|||
TD,20 µm TD,20 µm |
g | ASTM D1922 | |
MD,20 µm MD,20 µm |
g | ASTM D1922 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 f50 |
【新闻资讯】查看全部
国际能源署(IEA):全球能源需求复苏或延后至2025年
2020-10-17 搜料网资讯: 国际能源署(IEA)13日发布报告称,受疫情影响,预计今年世界石油需求同比下跌8%,每日需求减少800万桶,全球能源需求全面反弹可能要推迟至2025年。 在年度《世界能源 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |