牌号简介 About |
---|
GN2450具有高强度和高模量。它非常适合FPC滑块和IC插座,以及其他需要模数和尺寸精度的元件。 GN2450 features high strength and modulus. It is well suited for FPC sliders and IC sockets, as well as other components that require modulus and dimensional precision. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.73 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:1.0 mm MD:1.0 mm |
0.10 | % | ASTM D995 |
TD:1.00 mm TD:1.00 mm |
0.50 | % | ASTM D995 |
吸水率 Water absorption rate |
|||
40℃,95% RH 40℃,95% RH |
0.70 | % | ASTM D570 |
熔体质量流动速率 Melt Flow Rate |
|||
320℃,2.16kg 320℃,2.16kg |
15.00 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
熔融温度 Melting temperature |
℃ | ASTM D4591 | |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻 Volumetric resistance |
Ω.cm | ASTM D257 | |
绝缘强度 Insulation strength |
|||
|
KV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
10.0 GHz 10.0 GHz |
GHz | ASTM D150 | |
耗散因数 Dissipation factor |
|||
10 GHz 10 GHz |
GHz | ASTM D150 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
|
V-0 | UL 94 | |
|
V-0 | UL 94 | |
|
V-0 | UL 94 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3 mm 3 mm |
℃ | IEC 60695-2-12 | |
灼热丝相对温度 Relative temperature of heating wire |
|||
0.75mm 0.75mm |
℃ | IEC 60695-2-13 | |
1.50mm 1.50mm |
℃ | IEC 60695-2-13 | |
3.00mm 3.00mm |
℃ | IEC 60695-2-13 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 96 hrs |
3 750kgf |
【新闻资讯】查看全部
印度国内开展大规模运动抵抗一次性塑料的运用
2018-05-08 作为今年世界环境保护日(World Environment Day)纪念活动的举办国,印度将本次活动的主题定为“抵制塑料污染”。印度中央政府下达文件,要求各个邦、联邦属地和首都辖区开展大规模运动抵制一次性塑料的使用,并且按照文件要求禁止使用厚度小于50微米的塑料手提袋。 事实上,早在2016年,印度政府就已经禁止厚度小于50微米的聚乙烯塑料袋在全国范围内使用,但是在小型企业和供应商的阻力下,大多数地区都没能落实该政策。利益攸关方认为,缺乏替代方案是政策未能实施的障碍,但环保 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |