牌号简介 About |
---|
Westlake聚乙烯EF310是一种低密度聚乙烯,建议用于薄膜烘焙。这种材料具有优异的光学和加工性能。应用/使用面包袋软商品包装高清晰度纺织品包装袋 WESTLAKE polyethylene EF310 is a low-density polyethylene suggested for cast film bakery applications. This material has outstanding optical and processing properties. Application/Uses Bakery bags Soft goods packaging High clarity packaging Bags for textile items |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.924 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.2 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:32 µm,吹塑薄膜 1% secant, MD: 32 µ m, blow molded film |
186 | MPa | ASTM D882 |
1% 正割,TD:32 µm,吹塑薄膜 1% secant, TD: 32 µ m, blow molded film |
228 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,32 µm,吹塑薄膜 MD, fracture, 32 µ m, blow molded film |
23.4 | MPa | ASTM D882 |
TD,断裂,32 µm,吹塑薄膜 TD, fracture, 32 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,32 µm,吹塑薄膜 MD, fracture, 32 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,32 µm,吹塑薄膜 TD, fracture, 32 µ m, blow molded film |
% | ASTM D882 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,31.8 µm,吹塑薄膜 45 °, 31.8 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
31.8 µm,吹塑薄膜 31.8 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
落锤冲击 Drop hammer impact 2 |
|||
31.8 µm 31.8 µm 2 |
kN/m | ASTM D1709 |
备注 |
---|
2 Blown Film |
【新闻资讯】查看全部
美通胀上升或引发全球性风险
2021-07-12 搜料网资讯: 世界报业辛迪加网站7月9日发表题为《美国通胀上升引发全球性风险》的文章,作者系亚洲开发银行前首席经济学家、哥伦比亚大学商学院金融学和经济学教授魏尚进。文 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |