牌号简介 About |
---|
SABIC® LLDPE 430BE是一种丁烯线性低密度聚乙烯树脂。该材料,天然树脂,通常用于铸膜应用,提供良好的机械性能,刚度增强,而且能够获得高线速度。SABIC® LLDPE 430BE提供了适合于低凝胶水平的铸膜挤出的专用抗氧化包装。应用于不粘弹性流延膜、流延膜侧包封、中层卫生流延膜及产品的表皮层,通过硬度增强实现下测。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® LLDPE 430BE is a butene linear low density polyethylene resin. The material, natural resin, is typically used for cast film applications, offering good mechanically properties, stiffness enhancement and furthermore enables to gain high line speeds. SABIC® LLDPE 430BE is provided with a dedicated anti oxidant package suitable for cast film extrusion with low gel levels. Applications Skin layers for non-cling stretch cast film, cast film side encapsulation, mid layer hygienic cast film and product to realize downgauging by stiffness enhancement. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.930 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
4.2 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
Elastic Recovery(铸造薄膜,20.0 µm) Elastic Recovery (cast film, 20.0 µ m) |
45 | % | ASTM D5459 |
Protrusion Puncture Resistance - 铸造薄膜(20.0 µm) Corrosion Function Resistance - Cast thin film (20.0 µ m) |
0.500 | J | ASTM D5748 |
Stress Retention(铸造薄膜,20.0 µm) Stress Retention (cast film, 20.0 µ m) |
% | ASTM D5459 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,20 µm,铸造薄膜 45 °, 20 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
20.0 µm,铸造薄膜 20.0 µ m, cast thin film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
落锤冲击 Drop hammer impact |
|||
20.0 µm,铸造薄膜 20.0 µ m, cast thin film |
J/cm | ISO 7765-2 | |
撕裂强度 tear strength 1 |
|||
TD,20 µm TD,20 µm 1 |
kN/m | ISO 6383-2 | |
memo_intro memo_intro |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Cast Film |
【新闻资讯】查看全部
《农膜回收举动方案》 助力再生塑料回收
2017-06-02 农膜作为再生塑料回收成员的一份子,其科学回收问题也被提上了非常重要的地位。近日,农业部印发了《农膜回收行动方案》,加强农膜污染治理,提高废旧农膜资源化利用水平,提出到2020年,全国农膜回收网络不断完善,资源化利用水平不断提升,农膜回收利用率达到80%以上,“白色污染”得到有效防控。 膜料――回收难题之一 再生PE的主要回收来源为膜料、吹塑料、管道料、注塑料、拉丝料等,其中膜料的回收占比在再生PE中占主要地位,回收占比高达2 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |