牌号简介 About |
---|
MDPE HR 515是以己烯为共聚单体,采用浆环工艺生产的中密度聚乙烯。分子量分布广泛,加工性能优异。MDPE HR 515特别致力于高硬度薄膜应用,尤其是与LDPE和/或LLDPE的混合和/或共挤。MDPE HR 515适用于消费、工业、食品或卫生包装领域的许多薄膜应用。 MDPE HR 515 is a medium density polyethylene produced with hexene as co-monomer. It shows a broad molecular weight distribution ensuring outstanding processability. MDPE HR 515 is especially dedicated to high rigidity film applications, particularly in blend and/or coextrusion with LDPE and/or LLDPE. MDPE HR 515 is suited for many film applications, in the field of consumer, industrial, food or hygiene packaging. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.942 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
0.22 | g/10min | ISO 1133 |
190℃,21.6kg 190℃,21.6kg |
18 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲模量 Bending modulus |
810 | MPa | ISO 178 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 40 | µm | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,20 µm,吹塑薄膜 MD, yield, 20 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,20 µm,吹塑薄膜 TD, yield, 20 µ m, blow molded film |
MPa | ISO 527-3 | |
MD,屈服,40 µm,吹塑薄膜 MD, yield, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,40 µm,吹塑薄膜 TD, yield, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,20 µm,吹塑薄膜 MD, fracture, 20 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,20 µm,吹塑薄膜 TD, fracture, 20 µ m, blow molded film |
MPa | ISO 527-3 | |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,20 µm,吹塑薄膜 MD, fracture, 20 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,20 µm,吹塑薄膜 TD, fracture, 20 µ m, blow molded film |
% | ISO 527-3 | |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
ISO 7765-1 | ||
20 µm,吹塑薄膜 20 µ m, blow molded film |
g | ISO 7765-1 | |
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ISO 7765-1 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
MD:20 µm,吹塑薄膜 MD: 20 µ m, blow molded film |
N | ISO 6383-2 | |
TD:20 µm,吹塑薄膜 TD: 20 µ m, blow molded film |
N | ISO 6383-2 | |
MD:40 µm,吹塑薄膜 MD: 40 µ m, blow molded film |
N | ISO 6383-2 | |
TD:40 µm,吹塑薄膜 TD: 40 µ m, blow molded film |
N | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
车用塑料配件高端成型
2016-03-18 中国汽车工业的快速发展带动了车用塑料配件市场的发展,制造内外饰配件和关键汽车塑料部件的企业日益增多。同时,汽车轻量化技术的研究使得复合材料和创新材料应用趋于成熟。 汽车整车厂、零部件配套商对车用塑料配件制造工艺、品质要求提出了创新变革。近年来,一级配套商打造无人化、智能化工厂,对生产单元主体的注塑机稳定性提高了要求。促使车用塑料配件生产工艺朝着模具精密制造、精密注塑、后加工精密自动化的高端制造工艺方向发展。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |