牌号简介 About |
---|
交联聚乙烯绝缘和HFFR护套用阻燃垫层料。电缆和电线的垫层化合物,导体的最高工作温度为90°C。 OXPEKK® IG230C is a Polyetherketoneketone (PEKK) material filled with 30% carbon fiber. It is available in Europe or North America. Typical application of OXPEKK® IG230C: Medical/Healthcare |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.43 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.10 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
< 0.030 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2800 | MPa | ASTM D638 |
拉伸强度 tensile strength |
|||
断裂 fracture |
262 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
熔融温度 Melting temperature |
℃ | DSC | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
集泰股份荣获“绿+”企业认定 绿色实力得到认可
2021-07-11 搜料网资讯: 目前, 碳 达峰碳中和绿+企业已成为政府工作报告中的热词。 为充分发挥金融对环境治理和产业发展的引导、约束和杠杆作用,推动区域经济增长模式绿色转型和绿色技术 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |