Hapflex 700和800产品是一系列低危险、无色、高强度的弹性体,可用于65A至72D的肖氏硬度。Hapflex 700和800产品具有高拉伸强度、高撕裂强度和优异的延伸率。所有Hapflex 700和800产品均在室温下固化,可通过加热加速。700&800系列的另一个关键属性是所有组件的基色都是无色的。为了方便用户,Hapco设计了2种速度的系列产品,用户可以“定制”生产速度和固化时间。快速和正规的版本可以混合到用户定制凝胶时间和固化时间。Hapflex 700和800系列可用于机械、电气和机械/电气应用。此外,当与Hapco的单组分底漆200结合使用时,Hapflex 700和800产品显示出优越的浸水性能和优越的粘合性。 HAPFLEX 700 & 800 products are a series of low hazard, colorless, high strength, elastomers available in Shore hardnesses from 65A to 72D. HAPFLEX 700 & 800 products exhibit high tensile strength, high tear strength, and excellent elongation. All HAPFLEX 700 & 800 products cure at room temperature and can be accelerated with heat. Another key attribute of the 700 & 800 SERIES is that the base color of all components is colorless. For user convenience, HAPCO has designed this series in 2 speeds so the user can "customize" production rates and cure times. The fast and regular versions can be blended to user customize the gel time and cure time. HAPFLEX 700 & 800 SERIES can be used for mechanical, electrical, and mechanical/electrical applications. In addition, HAPFLEX 700 & 800 products show superior water immersion properties and superior adhesion when used in combination with Hapco's one part PRIMER 200. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.03 | g/cm³ | ASTM D4669 |
收缩率 Shrinkage rate |
|||
MD MD |
0.25 到 0.45 | % | ASTM D2566 |
Weight(per cubic inch) Weight(per cubic inch) |
17 | g | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
撕裂强度 tear strength 2 |
109 | kN/m | ASTM D624 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
80 | J/m | ASTM D256 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
J/m | ASTM D256 | |
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
25℃ 25℃ |
cP | ASTM D4878 | |
脱模时间 stripping time |
|||
21℃ 21℃ |
min | 内部方法 | |
胶凝时间 Gelation time 3 |
|||
25℃ 25℃ 3 |
min | ASTM D2971 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 100 g |
【新闻资讯】查看全部
方大锦化超额完成六月份消费经营义务
2017-07-04 6月份,是一年当中一个关键的时间节点。方大锦化化工科技股份有限公司各单位干部员工上下同欲,以“安全生产月”活动为契机,不断加大安全管理力度,紧密围绕生产经营指标,扎实推进精细化管理,降本增效工作,克服市场形势、环保压力带来的重重困难以及高温天气等不利因素的影响,始终保持良好发展态势,主导产品烧碱、环氧丙烷、聚氯乙烯产量分别完成作业计划的104.71%、106.88%、128.22%,发电量完成计划的122.78%,不仅为上半年生产经营的收官之战画上一个圆满的句号,同时又为建党96周年献上了 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |