牌号简介 About |
---|
SABIC® mLLDPE 8118是一种通过nexlene技术生产的乙烯-辛烯共聚物。它在广泛的通用和高性能LLDPE吹膜应用中表现良好,具有良好的加工性能。SABIC® mLLDPE 8118的典型应用包括层压膜、冷冻袋、液体袋、重型袋、工业衬垫、农业薄膜、拉伸罩、表面保护膜。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® SUPEER™ 8118 is an ethylene-octene copolymer produced via Nexlene™ Technology. It performs well in a wide range of general purpose and high performance LLDPE blown film applications and has good processablity. Application Typical applications for SABIC® SUPEER™ 8118 are lamination film, frozen bags, liquid pouches, heavy duty bags, industrial liner, agriculture film, stretch hood, surface protective film. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.1 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:50 µm,吹塑薄膜 1% secant, MD: 50 µ m, blow molded film |
140 | MPa | ASTM D882 |
1% 正割,TD:50 µm,吹塑薄膜 1% secant, TD: 50 µ m, blow molded film |
156 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 2 |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film 2 |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:50 µm,吹塑薄膜 MD: 50 µ m, blow molded film |
g | ASTM D1922 | |
TD:50 µm,吹塑薄膜 TD: 50 µ m, blow molded film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blown Film Melt Temperature Blown Film Melt Temperature |
℃ | ||
Blow(up Ratio) Blow(up Ratio) |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部
PC/ABS共聚物功能的四点要素
2016-04-18 PC/ABS共聚物是一种性能优良、价格低廉的工程塑料,在工业上应用广泛。合金中的ABS组分既能为PC/ABS合金提供较好的加工流动性,又可提高合金材料的耐低温性能。PC/ABS合金具有复杂的微观结构,其微观结构的改善能够显著提高合金的力学性能。 (1)原料性能 不同品牌的PC及ABS树脂共混的合金在性能上有较大的差异。高橡胶含量提高了PC/ABS体系的冲击强度,但大大损害了相态间互容行为,使合金的拉伸性能降低。因此,选用适当橡胶含量的ABS,不但可以使共混物 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |