牌号简介 About |
---|
Dryflex® 51712 SE:热塑性弹性体基材:TPS-SEBS硬度:60邵尔A工作温度范围:-50至+125°C(无应力材料)颜色:天然,但在任何阴影下都可以很容易着色呈现:在正常条件下储存时,可在无需预干燥的情况下处理的自由流动颗粒:卓越的臭氧-/U耐v性:优良的耐化学性:良好(不含有机溶剂、芳香族和植物油)回收利用率:100%可回收模具收缩率(线性):约0.75-2%,取决于细节形状和浇口连接的位置:PP、PE Dryflex 51712 SE: Thermoplastic Elastomer Base Material: TPS-SEBS Hardness: 60 Shore A Service Temperature Range: -50 to +125°C (unstressed material) Colour: Natural, but can easily be coloured in any shade Presentation: Free flowing pellets that can be processed without predrying when stored under normal conditions Weather Resistance: Excellent Ozone-/UV- Resistance: Excellent Chemical Resistance: Good (Excluding organic solvents, aromatic- and vegetable oils) Recycling: 100% recyclable Mould Shrinkage (linear): Appr. 0.75 - 2% depending on e.g. shape of the detail and placement of gate Bonds to: PP, PE |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.18 | g/cm³ | ISO 2781 |
收缩率 Shrinkage rate |
0.75 to 2.0 | % | 内部方法 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
7.00 | MPa | ISO 37 |
100% 应变 100% strain |
2.00 | MPa | ISO 37 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
600 | % | ISO 37 |
撕裂强度 tear strength 2 |
kN/m | ISO 34-1 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ISO 868 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
使用温度 Operating temperature 3 |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 方法:新月形试样 |
3 unstressed material |
【新闻资讯】查看全部
七小气法教您进步PVC塑料的耐热性
2016-08-03 1、PVC共聚物 PVC(氯乙烯)与其它单体共聚树脂的组成中若含有极性或大基团的组分,则共聚物的热变形温度相应增加,耐热性比PVC好,制得耐热制品。PVC的软化温度为78℃,而共聚物氯乙烯-偏氯乙烯、氯乙烯一甲基丙烯酸甲酯 、氯乙烯一丙烯睛的软化温度分别为100~130、85 、140~150℃。 2、PVC氯化 氯化聚氯乙烯是由PVC树脂氯化而制得的,其含氯量为 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |