牌号简介 About |
---|
尼龙NX1440是一种高粘度,快速循环成型树脂。结晶引发剂通过快速熔融设置提供快速成型周期。与传统尼龙模制品相比,NX1440模制品在水分平衡下具有更好的尺寸稳定性。尼龙NX1440在硬度和韧性之间提供了极好的平衡。 Nylene NX1440 is a high viscosity, fast cycling molding resin. Crystallization initiators provide fast molding cycles through rapid melt set-up. Parts molded from NX1440 have better dimensional stability at moisture equilibrium than parts molded from conventional nylon. Nylene NX1440 provides for an excellent balance between stiffness and toughness. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.14 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.90 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
1.5 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
75.2 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
25 | % | ASTM D638 |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
熔融温度 Melting temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
PC、PMMA、PET等常用透明原料的特性 注塑工艺详解
2019-01-30 由于塑料具有重量轻、韧性好、成型易、成本低等优点,因此在现代工业和日用产品中,塑料被越来越多的用来代替玻璃,特别是在光学仪器和包装工业的应用方面发展尤为迅速。 但是 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |