牌号简介 About |
---|
Ultramid® A3HG5是一种25%玻璃纤维增强注塑成型PA66级。典型应用包括高刚度和尺寸稳定性的机械部件和外壳。 Ultramid A3HG5 is a 25% glass fiber reinforced injection molding PA66 grade. Applications Typical applications include machinery components and housings of high stiffness and dimensional stability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.32 | g/cm³ | ASTM D792 |
密度 Density |
1.32 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
275℃,5 kg 275℃,5 kg |
50.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.30 | % | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
6.0 | % | ISO 62 |
饱和 saturated |
% | ASTM D570 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,50% RH Balance, 50% RH |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
断裂,-40℃ Fracture, -40 ℃ |
MPa | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂,-40℃ Fracture, -40 ℃ |
% | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃ 23℃ |
kJ/m² | ISO 180 | |
-40℃ -40℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ||
MD MD |
1/℃ | ||
MD MD |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
0.8 mm 0.8 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
1.50 mm 1.50 mm |
ohms·cm | ASTM D257 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.80 mm 0.80 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
片面解析塑料造粒机的行业展开方向
2018-05-28 面对严峻的能源与环境挑战,中国最近以全面、协调、可持续的科学发展观为指导思想,制定了至2020年的中长期能源科技发展战略与发展规划。 这一能源环境发展战略的制定,也为中国塑料造粒机技术的发展指明了方向,探索塑料造粒机技术的新型发展道路势在必行。与工农业生产中的其它操作环节相比,塑料造粒机过程的节能与防治污染任务尤其迫切。 |
片面解析塑料造粒机的行业展开方向 应对不容乐观的电力能源与自然环境挑戰,中国近期以全方位、融洽、可持续性的科学研究发展观为指导方针,制订了至今年的中远期能源科技公司发展发展战略与发展整体规划。 这一电力能源自然环境发展发展战略的制订,也为中国塑料造粒机技术的发展指明了方向,探索塑料造粒机技术的新式发展路面刻不容缓。与工业和农业生产制造中的其他实际操作阶段对比,塑料造粒机全过程的环保节能与预防污染每日任务特别是在急切。
塑料造粒机工作涉及到社会经济的普遍行业,它不但是大量工业和农业商品必不可少的基础生产制造阶段,塑料造粒机也是中国的能耗种植大户,常用电力能源占社会经济总耗能的12%上下。此外,塑料造粒机全过程导致的污染又经常是中国自然环境污染的关键来源于,塑料造粒机技术的发展同全部社会经济的发展有十分密不可分的关联。 最先,塑料造粒机实际操作涉及到的行业极其普遍,而中国的塑料造粒机耗能占全部工业生产耗能的占比基本上比美国高一半,做到12%. 次之,塑料造粒机对自然环境的污染也相当严重。在运用较广的各种基本塑料造粒机机器设备中,有四分之三之上是暖风塑料造粒机,这类塑料造粒机机器设备对自然环境的污染十分比较严重,针对塑料造粒机系统软件原煤炉的更新改造已变成急需解决的关键课题研究。 提升塑料造粒机全过程的电力能源利用率和预防对自然环境的污染是紧密联系的。降低一亿吨标煤的能耗,在中国就可以降低6400万吨级之上CO2和SO2的排污,其环境保护经济效益十分明显。 因而,在探索塑料造粒机技术的新式发展路面时,务必对能耗等级、环境保护及其商品的品质开展综合性考虑到,以求取全方位、融洽和可持续性地发展。要执行高效率与翠绿色塑料造粒机的发展发展战略,最先要走节约型社会发展路面,变单一粗放式塑料造粒机为组成、全智能塑料造粒机。 不但要从塑料造粒机加工工艺上开展压根更新改造,也要开展全方位、多层面的环保节能技术更新改造,全力发展运用可再生资源与工业生产余热回收的塑料造粒机技术。从政府部门方面,要创建与健全塑料造粒机机器设备的考核评价规则与国家标准,创建宏观经济政策与销售市场调节机制,加速塑料造粒机技术的升级换代。 来源于:中国塑料机械网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
- 汽车轮速传感器
- 2019-09-19 0
- Ultramid® A3HG5是一种25%玻璃纤维增强注塑成型PA66级。典型应用包括高刚度和尺寸稳定性的机械部件和外壳。
- 阅读全文
汽车轮速传感器
抱歉!暂无数据。