牌号简介 About |
---|
andur M-11是一种MDI酯预聚物,在加工过程中,密切关注处理程序和配方,生产高品质的弹性体。这些弹性体在动态应用中表现很好。 |
技术参数 Technical Data | |||
---|---|---|---|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
屈服 yield |
42.1 | MPa | ASTM D412 |
100% 应变 100% strain |
7.93 | MPa | ASTM D412 |
200% 应变 200% strain |
17.2 | MPa | ASTM D412 |
300% 应变 300% strain |
27.6 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
410 | % | ASTM D412 |
压缩形变 Compression deformation |
% | ASTM D395 | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
储存稳定性 storage stability |
min | ||
脱模时间 stripping time |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A Shaw's A |
ASTM D2240 | ||
邵氏 D Shaw's D |
ASTM D2240 | ||
压缩强度 compressive strength |
ASTM D695 | ||
2% 应变 2% strain |
MPa | ASTM D695 | |
5% 应变 5% strain |
MPa | ASTM D695 | |
10% 应变 10% strain |
MPa | ASTM D695 | |
15% 应变 15% strain |
MPa | ASTM D695 | |
20% 应变 20% strain |
MPa | ASTM D695 | |
25% 应变 25% strain |
MPa | ASTM D695 | |
50% 应变 50% strain |
MPa | ASTM D695 | |
泰伯耐磨性 Taber abraser |
mg | ASTM D1044 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
环保、跌价潮再次袭来,2017改性塑料的开展和机遇!
2017-02-24 2017年的塑料市场命运多舛,涨价的风波还没消停,环保又开始了,面对这样的情况,2017年的改性市场将如何发展? 我国改性塑料行业存在较大发展空间。数据显示,中国塑料总产量从2004年的近1800万吨上涨至2016年的近8000万吨,改性化率也从8%增长到19%。 然而,相比全球40%的改性塑料用于汽车行业,中国仅10%左右。衡量一个国家塑料工业发展水平的重要指标――塑钢比,我国仅为30∶70,不及世界平均的50∶50,更远不及发达国家如美国的70:30和德 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |