牌号简介 About |
---|
PA 6,非增强,挤压,中等粘度,滑动剂,成核 Durethan® B38FKA 000000 (Dry) PA 6, non-reinforced, extrusion, medium viscosity, slip agent, nucleated, suitable for food-contact Durethan® B38FKA 000000 PA 6, non-reinforced, extrusion, medium viscosity, slip agent, nucleated, suitable for food-contact Durethan® B38FKA 000000 PA 6, non-reinforced, extrusion, medium viscosity, slip agent, nucleated, suitable for food-contact |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.14 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.70 | g/cm³ | ISO 60 |
熔体体积流动速率 Melt Volume Rate |
|||
235℃,2.16 kg 235℃,2.16 kg |
5.00 | cm³/10min | ISO 1133 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
10 | % | ISO 62 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
3.0 | % | ISO 62 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B120 B120 |
℃ | ISO 306/B120 | |
熔融温度 Melting temperature 5 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index 5 |
% | ISO 4589-2 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
ISO 1874 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 2 |
|||
23℃ 23℃ 2 |
MPa | ISO 178-A | |
弯曲强度 bending strength 2 |
|||
3.20%应变 3.20% strain |
MPa | ISO 178-A | |
弯曲应变 Bending strain 3 |
% | ||
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 Pull Rate: 2 mm/min; 50% RH |
4 10°C/min |
5 程序 A |
【新闻资讯】查看全部
贵港市联合开展废塑料等再生利用行业清算整理行动
2017-11-21 近期,由贵港市环境保护局、贵港市发展和改革委员会、贵港市工业和信息化委员会、贵港市公安局、贵港市商务局、贵港市工商行政管理局等部门联合开展贵港市电子废物、废轮胎、废塑料、废旧衣服、废家电拆解等再生利用行业清理整顿行动,取缔一批污染严重、群众反映强烈的非法加工利用小作坊、“散乱污”企业和集散地,并对一批企业进行规范引导。 一是依法取缔一批污染严重的非法再生利用企业。环境保护部门和工商部门联合开展执法行动,现场排查港北区、桂平市、平南县等10家废塑料加工利用企业,对排查过程中发 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |