牌号简介 About |
---|
Ebalta GH 767 / GL是一种双组分环氧树脂,在室温下固化。由于其良好的可浇铸性,该产品是多功能的。使用我们的皮肤友好型硬化剂GL,您可以获得40-50 mm的铸件厚度。应用铸造型芯盒型板负极控制铸件模型探针用于修整原型样品性能和易铸性高达50 mm尺寸稳定 ebalta GH 767/GL is a two-components epoxy resin which cures at room temperature. Due to its good castability this product is versatile. With our skin friendly hardener GL you get casting thicknesses of 40-50 mm. Applications Foundry patterns Core boxes Pattern plates Negatives Control castings Mould probes for trimming of prototypes Samples Properties workable castable up to 50 mm dimensionally stable |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
3.1 到 5.1 | kJ/m² | ISO 179 |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
20℃ 20℃ |
1.90 到 2.10 | g/cm³ | |
粘度 viscosity |
|||
25℃ 25℃ |
4.0 到 5.0 | Pa·s | |
固化时间 Curing time |
|||
20℃ 20℃ |
12 到 16 | hr | |
储存稳定性 storage stability 2 |
|||
20 ℃ 20 ℃ 2 |
25 到 35 | min | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 7619 | ||
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Martens Temperature Martens Temperature |
℃ | DIN 53458 | |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 200 g |
【新闻资讯】查看全部
隆华新材创业板上市 募资2.7亿元用于聚醚多元醇扩建
2021-11-10 搜料网资讯: 11月9日,山东隆华新材料股份有限公司(以下简称隆华新材)正式在深圳证券交易所创业板上市,股票代码为002195.SZ。 招股说明书显示,隆华新材主要从事聚醚多元醇( |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |